Stress-Strain Behavior of Cementitious Materials with Different Sizes

Zhou, Jikai; Qian, Pingping; Chen, Xudong

doi:https://doi.org/10.1155/2014/919154

The Scientific World Journal

On this page

Abstract Introduction Discussion Conclusions References Copyright Related Articles

Research Article | Open Access

Volume 2014 | Article ID 919154 | https://doi.org/10.1155/2014/919154

Stress-Strain Behavior of Cementitious Materials with Different Sizes

Jikai Zhou,¹Pingping Qian,¹and Xudong Chen¹

Academic Editor: A. T. Marques, C. Rambo

Received30 Dec 2013

Accepted19 Feb 2014

Published13 Mar 2014

Abstract

The size dependence of flexural properties of cement mortar and concrete beams is investigated. Bazant’s size effect law and modified size effect law by Kim and Eo give a very good fit to the flexural strength of both cement mortar and concrete. As observed in the test results, a strong size effect in flexural strength is found in cement mortar than in concrete. A modification has been suggested to Li’s equation for describing the stress-strain curve of cement mortar and concrete by incorporating two different correction factors, the factors contained in the modified equation being established empirically as a function of specimen size. A comparison of the predictions of this equation with test data generated in this study shows good agreement.

1. Introduction

It is widely believed that the true fracture properties of concrete structures can be unequivocally determined only by means of uniaxial tensile stress [1]. Unfortunately, tensile tests are difficult to carry out in standard laboratories, either with fixed or rotating boundary conditions. Therefore, the flexure strength, measured for beams in either three- or four-point bending, turns out to be an experimentally convenient measure of strength owing to the relative simplicity of these results [2–9].

It is important to consider the effect of size while estimating the ultimate strength of a concrete member under various loading conditions. Presently, most design codes for concrete structures do not consider the effect of size. Since quasibrittle materials fail by formation of cracks, size effect has to be implemented. The influence of specimen diameter [10, 11] and slenderness ratio [12–14] on the compressive strength of concrete has been reported by many investigators. Less is known about the size effects when passing from the uniaxial tension domain into the flexural tension range. Four-point bending test was analyzed theoretically by Ghaemmaghami and Ghaemian [15] using a cohesive crack model. The results obtained with the model showed that the flexural strength of quasibrittle materials such as concrete, ceramics, and rocks is a decreasing function of the specimen size, whose value decreases as the size increases. Vořechovský [16] also noted that the tensile strength was different depending on the type of loading applied to specimens of the same volume and geometry. Experiments show that the average tensile strength computed from four-point bending beams are increased by 200 percent and by 220 percent in three-point bending from what is measured in direct tension. Experiments on notched specimens of homothetic sizes made of concrete, rocks, and ceramics by Bazant et al. [17, 18] and Man and Van Mier [19] also demonstrate that the nominal tensile and shear strengths depend on the size of the specimens. All these experiments show two key points: the flexural strength of cement-based materials as predicted by elasticity or limit analysis is a function of the volume of the specimen and of the stress field in the structure. Part of this size effect can be attributed to the existence of initial defects in the material before any stress is applied to it, and the fracture toughness measure from notched specimens also varies with the size of the structure. Failure in these materials is often the result of progressive microcracking in a fracture process zone whose size is related to the size of inhomogeneities or aggregates. From the literature it can be found that there are many studies on mechanical characteristics of notched beams and only a few on the notchless beams. The present study is aimed at documenting the effects of size in notchless cement mortar and concrete beams.

The size effects on the strength of concrete materials have been generally explained as a macroscopic phenomenon resulting from internal microscopic defects such as microcracks and inclusions in the material. Mazars et al. [20], Kameswara Rao and Swamy [21], and Kumar and Barai [22] have tried to apply some theoretical approaches to clarify the size effect on the strength of concrete. Most of the researchers have set up the theories based on the assumption that the size effect in strength is related to the quantity of defects in the specimen, that is, the size of specimen. Intensive studies on the strength of concrete in the last decades have clarified that the size effect on strength is related to primarily to a relatively large fracture propagation process (FPZ) in concrete [23]. Nonlinear fracture models, that is, the Fictitious Crack Model by Hillerborg et al. [24], the Crack Band Model by Bazant [25], and the Two-Parameter Model by Jenq and Shah [26], have been applied to the analysis and prediction of size effects in concrete strength. Successively, Carpinteri et al. [27] proposed the Multi-Fractal Scaling Law (MFSL), valid for initially integer specimens and components. However, such investigations have often been restricted to strength and the deformation has not been reported.

Knowledge of the stress-strain relationship of concrete is vital to achieve a rational design of structures and structure components involving concrete. The nonlinear stress-strain behavior, size-dependent strength, fracture mode transition, and other phenomena are not adequately explained by the classical concepts of the mechanical behavior of materials and mechanics of fracture [28–30]. Enquiry into such aspects of the behavior of materials is essential in assessing the material properties of engineering importance, correlating the observations from tests on modes to those of prototypes, and so forth. With regard to the stress-strain relationship, studies reporting the size effect are very scarce.

In this paper, the authors discuss the size effects on cement mortar and concrete flexural behavior quantitatively. The equations to estimate stress-strain curves were also proposed. Results of the investigation on the validity of the existing models are reported as well. This paper brings together the results of past studies and the results of new experiments and interpretations.

2. Experimental Program

2.1. Materials and Specimens

Ordinary Portland cement (OPC) was used in the production of cement mortar specimens. The cement was the most widely used cement in general concrete construction works in China. The fine aggregate was river sand consisting mainly of quartz, with 10 percent feldspar. The gradation test showed that the particle size of the sand was continuously distributed within the range of 0.4–2.5 mm with 80% of sand. The water-cement ratio () 0.4 and sand-cement ratio () 2 were used for cement mortar. The cement mortar also has the same compositions as the mortar phase in the concrete. When tested separately, it provides a mean for obtaining the response of the mortar in concrete. It must be pointed out that the in situ properties of mortar phase may not exactly the same as those of the pure mortar; especially the degree of porosity in the matrix could be different from that of the pure mortar [31]. The crushed granite was used as the aggregate of concrete and its maximum grain size was 15 mm. The aggregate-cement ratio () 1.5 was used for concrete.

Test specimens of three different sizes were cast. Their dimensions were (width × depth × length): mm, tested on a 120 mm span; mm, tested on a 300 mm span; and mm, tested on a 450 mm span. Figure 1 shows the three different size concrete specimens used in this investigation. Three specimens of each size were cast. The forms were covered with wet burlap for the first two days; the specimens were then cured in the ambient laboratory environment for a further 34 to 36 days until they were tested. Three companion 150 cubes were also cast and subjected to the same curing. They were tested at an age of 38 days, yielding an average compressive strength of 52.3 MPa for cement mortar and 65.61 MPa for concrete.

2.2. Four-Point Loading Tests

As aforementioned, in order to study the influence of specimen size on flexural properties of cement mortar and concrete, four-point bending tests on beams were conducted. The testing was conducted using a dynamic loading system that applied a programmable controlled loading. All these tests were performed with a closed loop servo-controlled stiff testing machine. The load was applied at an approximately constant deformation rate of 0.25 kN/s. The test setup is shown in Figure 2. The width of the support was kept constant as it was not thought that this would have any influence on the results. The measurement system consists of a strain amplifier, a tape recorder, and an intelligent signal processor. A 10⁴ Hz sampling frequency can be achieved. Eleven pairs of foil strain gages, 5 mm in width and 50 mm in width, were used to monitor the strain histories. They were crossly glued onto the faces of the specimen. Each specimen was removed from the moist room 2 days before testing. Typical load-time curve for a concrete beam test at the loading is shown in Figure 3. This illustrates that the linearity of loading was acceptable and that failure was easily recognized. Figure 4 shows the typical flexural failure mode of concrete beams; the failure location of all concrete beams is at the midspan.

3. Test Results and Discussion

The discussion of the results is organized as follows. First we present and describe the strength results obtained from the tests. Then we proceed to discuss the size effect in stress-strain curves. In addition, the test results were compared with existing scaling laws.

3.1. Size Effect on Strength

The flexural strength of cement mortar and concrete measured from different sizes of beams are shown in Figures 5 and 6. The flexural strength of both cement mortar and concrete decreases with the specimen size increases, which is similar to the trend observed by others [23, 27, 29, 32]. But a strong size effect in flexural strength is found in cement mortar than in concrete. Kani [33] was one of the first to demonstrate the size effect in concrete structures. It has been shown that the strength of similar concrete beams decreases with increasing beam depth. Due to the fracture in a structural element being driven by storing energy released from the whole structure, this size effect can be well interpreted by fracture mechanics. The fact that the strength of brittle materials is affected by the presence of defects is first suggested by Griffith [34]. Due to his conclusion, it can be expected that the value of the ultimate strength will depend upon the size of specimen. As specimen size increases, the strength is expected to be decreased since the probability of presence of weak links is increasing. Traditionally, the size effect in fracture of concrete structural elements has been explained as Weibull’s theory [35]. He showed that if tensile tests are performed on two geometrically similar specimens with different volumes, the corresponding ultimate strengths are different. It has also been concluded by other researchers [36–40].

Glucklich and Cohen [41] attribute the decrease in the failure strength with increased size to a strain energy mechanism. They describe the mechanism of stable crack growth based on the elastic energy stored within a specimen, with the amount of energy stored being correlative with specimen size. A sudden drop in the resistance of the specimen is followed by a decrease in the driving force; the energy rate exceeds that of energy demand; equilibrium breaks down; and accelerated failure takes place. When a system is overstocked with strain energy due, say, to the largeness of the specimen, any sudden drop in energy demand creates an excess of energy released. This then takes the form of kinetic energy which then advances fracture, favoring the conditions of unstable crack propagation. This mechanism may be plausible in the case of concrete materials, because Glucklich and Cohen [41] do not account for the constant maximum strength values for specimen above a certain size.

The other explanation of the size effect on flexural strength is to be found in the theory of quasibrittle fracture, describing materials of heterogeneous microstructure in which the formation of distinct fractures is preceded by distributed cracking. The failure of a beam begins by distributed cracking that develops in a boundary layer. The thickness of this layer for different beam sizes is about the same, provided the same concrete is considered. Hillerborg et al. [24] showed by numerical calculations that the stress distribution at the peak load has a maximum that lies at a certain distance from the tensile face. This distance is determined by the softening stress-displacement relation to the cohesive (fictitious) crack model. Dyskin et al. [42] and Karihaloo et al. [43] also demonstrated that numerical calculations based on the cohesive model can match the test results on the influence of beam size.

Some relationships involving strength and size of engineering materials have been reported in the literature. Historically, several general types of model have been developed for cement-based materials. As stated above, the aim of the investigation is to judge the range of applicability of the various size effect formulae available in the literature.

On the basis of the experimental results, an empirical expression was proposed by Xu and He [44], relating the nominal flexural strength to the depth of of the specimens: where is the uniaxial tensile strength, which in our cases we take as the strength that is obtained from the direct tension test in this investigation (as shown in Figure 7). Note that, according to (1), the flexural strength of very deep beams () becomes smaller than . Note also that these arguments would imply that the nominal flexural strength increases if applied compressive loads act upon the beam, thus reducing the size of the tension zone.

Based on a similar strain-gradient approach, a size dependent empirical relationship for the flexural strength has been specified in the CEB-FIP Model Code 1990 [45] and is given by where is a reference size equal to 100 mm. Note that (2) comes from experimental observations and no consideration is given to the role of the microstructure, whereas aggregate interlocking is explicitly taken into account in the codes when dealing with the ultimate shear strength.

In the analysis of the flexural strength of concrete, Rokugo et al. [46] employed a finite element method incorporating tension softening. It was found that the flexural strength can be expressed as a function of the ratio of the beam depth to the characteristic length. Based on the results, the authors proposed an equation to estimating the flexural strength of specimens with different sizes as follows: where is Hillerborg’s characteristic length [24] and . For cement-based materials, .

According to Bazant [25], the size effect in solids is a smooth transition from the strength criterion of plasticity (applicable to small size specimens) to the crack size dependence of linear elastic fracture mechanics (LEFM) (as seen in larger specimens). The failure stress of s series of geometrically similar specimens of concrete is described by the following infinite series: where , , and () are empirical constants obtained from experimental data. For the size rang up to , the infinite series, (4), may be truncated to the first two terms. Thus, Bazant’s size effect law (BSEL) reduces to

In fact, (5) has been established by Taylor’s expansion from this asymptotic limit [25]. The positive coefficients and in (5) are related to the specific fracture energy and the fracture process zone (FPZ) size of a very large structure (), as well as to the nondimensional geometry factor and its first derivative. The geometry factor depends on the notch to depth ratio and the geometry of the test specimen.

By considering a constant maximum flaw size, as is likely to occur in real materials, Kim and Eo [47] proposed the modified size effect law by adding to the BSEL the size-independent strength (=):

Chen et al. [9] used the concept of self-similar morphologies with noninteger dimensions called fractals to describe the microstructure of quasibrittle materials such as cement-based materials. With an increase in the scale of observation, the topological fractality is thought to vanish. On the bases of this hypothesis, the following multifractal scaling law (MFSL) was proposed: where is the characteristic length of the material.

Karihaloo et al. [48], using the stress intensity factor (SIF) and the fictitious crack concepts, proposed the formula: where is constant. This formula is, however, unlikely to be applicable when is small, which is a consequence of several approximations and assumptions made in its derivation. The constant in (8) is also related to the FPZ size of a very large structure and to the nondimensional geometry and its first derivative.

By plotting these relationships against the experimental results in this study (Figure 8), the correspondence with the data obtained can then be appreciated. From literature review and Figure 8, it can be found that the empirical model agrees well with their respective experimental data and less well with the experimental data obtained by other authors, because each proposed equation was obtained by using a regression analysis to interpolate their own experimental data. Moreover, appreciable difference arises between the curves, either in the case of the smaller, or, which is more important, in the case of larger beam sizes (Figure 8). Note that Bazant’s size effect law and the modified size effect law proposed by Kim and Eo [47] are in agreement with the test results of this investigation. The same results have also obtained by other researchers [32, 49].

(a)

(b)

3.2. Stress-Strain Curves

The stress-strain curves of cement mortar and concrete with different sizes are shown in Figures 9 and 10. It is seen that the stress-strain curves of the three sizes of specimens behave considerably different. It is evident from Figures 9 and 10 that the critical strain at the peak load is more or less constant and independent of specimen size. This indicates that a major source for the size effect of strength for cement-based materials may actually be the material’s modulus of elasticity. Strength being a macroscopic measure for the material is probably influenced by the fluctuation of the modulus of elasticity, which in turn is influenced by the aggregate size to specimen size ratio [12, 16]. Microscopically, the cement-based material of each mix is identical, independent of specimen size. Thus, the characteristic strain at peak load should also be independent of specimen size, as it appears to be. The strain invariance in combination with the variance of the modulus of elasticity with specimen size appears to be a possible explanation of the so-called size effect of material strength.

(a)

(b)

(c)

(a)

(b)

(c)

4. Modeling Stress-Strain Relationship Based on Continuous Damage Mechanics

Damage mechanics has become a powerful tool for the modeling of the nonlinear behavior of materials subjected to a progressive microcracking process. The theory itself was initially developed in 1958 [50], and, in the particular case of concrete, different constitutive models based on scalar, tensorial damage concepts have been formulated since then [51–53].

Among many types of concrete damage models at hand, one established model [54] was taken, where the damage variable is defined as in which is the area of the cross section with damage and is the area without damage. Moreover, the effective stress is defined as follows: where is the macroscopic stress.

According to the equivalent strain principle in damage mechanics, the damage constitutive relationship of concrete was established by Li et al. [54] as where is threshold strain, below which no damage occurs; is the elastic modulus (GPa); and , are damage parameters of the stress-strain curve.

The effect of specimen size was taken into account by assuming that the threshold strain (, 10⁻⁶), and the elastic modulus (, GPa) are size-dependent. For cement mortar, , and ; for concrete, , and . The following relationships were derived from the experimental results: for cement mortar, for concrete,

The predictions of the analytical model thus computed are compared with the experimental data for different sizes of cement mortar and concrete in Figures 11 and 12. It may be seen that the theoretical predictions are in good agreement with the experimental curves.

(a)

(b)

(c)

(a)

(b)

(c)

5. Conclusions

In this study, the flexural behavior of cement mortar and concrete with different sizes were investigated. From the test results, the following conclusions can be drawn.(1)Test results of flexural strength show size effect. Large specimens resist less in terms of stress than the smaller ones. A strong size effect in flexural strength is found in cement mortar than in concrete. The size effect in flexural strength is compared with existing scaling laws; it is found that Bazant’s size effect law and the modified size effect law proposed by Kim and Eo are in agreement with the test results.(2)A modification has been suggested to Li’s equation for describing the stress-strain curve of cement mortar and concrete by incorporating two different correction factors, the factors contained in the modified equation being established empirically as a function of specimen size. A comparison of the predictions of this equation with test data generated in this study shows good agreement.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgment

The authors are grateful to the National Natural Science Foundation of China (Grant no. 51178162) for the financial support.

References

Q. Li and F. Ansari, “High-strength concrete in uniaxial tension,” ACI Structural Journal, vol. 97, no. 1, pp. 49–57, 2000.
View at: Google Scholar
A. J. Raphael, “Tensile strength of concrete,” ACI Journal Proceedings, vol. 81, pp. 158–165, 1984.
View at: Google Scholar
S. Wu, X. Chen, and J. Zhou, “Tensile strength of concrete under static and intermediate strain rates: correlated results from different testing methods,” Nuclear Engineering and Design, vol. 250, pp. 173–183, 2012.
View at: Google Scholar
A. Carpinteri, B. Chiaia, and G. Ferro, “Scale dependence of tensile strength of concrete specimens: a multifractal approach,” Magazine of Concrete Research, vol. 50, no. 3, pp. 237–246, 1998.
View at: Google Scholar
X. Chen, S. Wu, and J. Zhou, “Strength values of cementitious materials in bending and in tension test methods,” Journal of Materials in Civil Engineering, vol. 26, pp. 484–490, 2014.
View at: Google Scholar
X. Chen, S. Wu, and J. Zhou, “Analysis of mechanical properties of concrete cores using statistical approach,” Magazine of Concrete Research, vol. 65, pp. 1463–1471, 2013.
View at: Google Scholar
X. Chen, S. Wu, J. Zhou, Y. Chen, and A. Qin, “Effect of testing method and strain rate on stress-strain behavior of concrete,” Journal of Materials in Civil Engineering, vol. 25, pp. 1752–1761, 2013.
View at: Google Scholar
X. Chen, S. Wu, and J. Zhou, “Experimental and modeling study of dynamic mechanical properties of cement paste, mortar and concrete,” Construction and Building Materials, vol. 43, pp. 419–430, 2013.
View at: Google Scholar
X. Chen, S. Wu, and J. Zhou, “Experimental study and analytical formulation of mechanical behavior of concrete,” in Construction and Building Materials, vol. 43, pp. 662–670, 2013.
View at: Google Scholar
P. Nallathambi, B. L. Karihaloo, and B. S. Heaton, “Various size effects in fracture of concrete,” Cement and Concrete Research, vol. 15, no. 1, pp. 117–126, 1985.
View at: Google Scholar
P.-C. Aitcin, B. Miao, W. D. Cook, and D. Mitchell, “Effects of size and curing on cylinder compressive strength of normal and high-strength concretes,” ACI Materials Journal, vol. 91, no. 4, pp. 349–354, 1994.
View at: Google Scholar
Y. Tanigawa and K. Yamada, “Size effect in compressive strength of concrete,” Cement and Concrete Research, vol. 8, no. 2, pp. 181–190, 1978.
View at: Google Scholar
M. S. Chin, M. A. Mansur, and T. H. Wee, “Effects of shape, size, and casting direction of specimens on stress-strain curves of high-strength concrete,” ACI Materials Journal, vol. 94, no. 3, pp. 209–218, 1997.
View at: Google Scholar
J. R. del Viso, J. R. Carmona, and G. Ruiz, “Shape and size effects on the compressive strength of high-strength concrete,” Cement and Concrete Research, vol. 38, no. 3, pp. 386–395, 2008.
View at: Publisher Site | Google Scholar
A. Ghaemmaghami and M. Ghaemian, “Large-scale testing on specific fracture energy determination of dam concrete,” International Journal of Fracture, vol. 141, no. 1-2, pp. 247–254, 2006.
View at: Publisher Site | Google Scholar
M. Vořechovský, “Interplay of size effects in concrete specimens under tension studied via computational stochastic fracture mechanics,” International Journal of Solids and Structures, vol. 44, no. 9, pp. 2715–2731, 2007.
View at: Publisher Site | Google Scholar
Z. P. Bazant and Z. Li, “Modulus of rupture: size effect due to fracture initiation in boundary layer,” Journal of Structural Engineering, vol. 121, no. 4, pp. 739–746, 1995.
View at: Publisher Site | Google Scholar
Z. P. Bazant, Y. Zhou, D. Novák, and I. M. Daniel, “Size effect on flexural strength of fiber-composite laminates,” Journal of Engineering Materials and Technology, vol. 126, no. 1, pp. 29–37, 2004.
View at: Publisher Site | Google Scholar
H.-K. Man and J. G. M. Van Mier, “Damage distribution and size effect in numerical concrete from lattice analyses,” Cement and Concrete Composites, vol. 33, no. 9, pp. 867–880, 2011.
View at: Publisher Site | Google Scholar
J. Mazars, G. Pijaudier-Cabot, and C. Saouridis, “Size effect and continuous damage in cementitious materials,” International Journal of Fracture, vol. 51, no. 2, pp. 159–173, 1991.
View at: Publisher Site | Google Scholar
C. V. S. Kameswara Rao and R. N. Swamy, “A statistical theory for the strength of concrete,” Cement and Concrete Research, vol. 4, no. 4, pp. 669–681, 1974.
View at: Google Scholar
S. Kumar and S. V. Barai, “Size-effect of fracture parameters for crack propagation in concrete: a comparative study,” Computers and Concrete, vol. 9, no. 1, pp. 1–9, 2012.
View at: Google Scholar
T. Tang, S. P. Shah, and C. Ouyang, “Fracture mechanics and size effect of concrete in tension,” Journal of Structural Engineering, vol. 118, no. 11, pp. 3169–3185, 1992.
View at: Google Scholar
A. Hillerborg, M. Modéer, and P.-E. Petersson, “Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements,” Cement and Concrete Research, vol. 6, no. 6, pp. 773–781, 1976.
View at: Google Scholar
Z. P. Bazant, “Size effect in blunt fracture: concrete, rock, metal,” Journal of Engineering Mechanics, vol. 110, no. 4, pp. 518–535, 1984.
View at: Google Scholar
Y. S. Jenq and S. P. Shah, “A two parameter fracture model for concrete,” Journal of Engineering Mechanics, vol. 111, no. 10, pp. 1227–1241, 1985.
View at: Google Scholar
A. Carpinteri, B. Chiaia, and G. Ferro, “A new explanation for size effects on the flexural strength of concrete,” Magazine of Concrete Research, vol. 48, no. 5, pp. 45–53, 1996.
View at: Google Scholar
H.-K. Man and J. G. M. Mier, “Size effect on strength and fracture energy for numerical concrete with realistic aggregate shapes,” International Journal of Fracture, vol. 154, no. 1-2, pp. 61–72, 2008.
View at: Publisher Site | Google Scholar
Z. Zhao, S. H. Kwon, and S. P. Shah, “Effect of specimen size on fracture energy and softening curve of concrete: part I. Experiments and fracture energy,” Cement and Concrete Research, vol. 38, no. 8-9, pp. 1049–1060, 2008.
View at: Publisher Site | Google Scholar
R. Ince, “Determination of concrete fracture parameters based on two-parameter and size effect models using split-tension cubes,” Engineering Fracture Mechanics, vol. 77, no. 12, pp. 2233–2250, 2010.
View at: Publisher Site | Google Scholar
H. Zhao, W. Sun, X. Wu, and B. Gao, “Effect of initial water-curing period and curing condition on the properties of self-compacting concrete,” Materials and Design, vol. 35, pp. 194–200, 2012.
View at: Publisher Site | Google Scholar
F. P. Zhou, R. V. Balendran, and A. P. Jeary, “Size effect on flexural, splitting tensile, and torsional strengths of high-strength concrete,” Cement and Concrete Research, vol. 28, no. 12, pp. 1725–1736, 1998.
View at: Google Scholar
G. N. Kani, “How safe are our large concrete beams?” ACI Journal Proceedings, vol. 56, pp. 1469–1479, 1967.
View at: Google Scholar
A. A. Griffith, “The phenomena of rupture and flow in solids,” Philosophical Transactions of the Royal Society A, vol. 221, pp. 163–198, 1920.
View at: Google Scholar
W. Weibull and S. Sweden, “A statistical distribution function of wide applicability,” Journal of Applied Mechanics, vol. 18, pp. 293–297, 1951.
View at: Google Scholar
B. Cotterell, Y.-W. Mai, and K. Y. Lam, “Statistics and size effect in cementitious materials,” Cement and Concrete Research, vol. 25, no. 2, pp. 408–416, 1995.
View at: Google Scholar
G. Yang and H. Hikosaka, “Crack length and specimen size influences on fracture strength of brittle materials,” Construction and Building Materials, vol. 10, no. 8, pp. 565–570, 1996.
View at: Publisher Site | Google Scholar
V. Koç and S. Şener, “Size effect in normal- and high-strength concrete with different notches under the axial load,” Journal of Materials in Civil Engineering, vol. 21, no. 9, pp. 433–445, 2009.
View at: Publisher Site | Google Scholar
R. Ince and E. Arici, “Size effect in bearing strength of concrete cubes,” Construction and Building Materials, vol. 18, no. 8, pp. 603–609, 2004.
View at: Publisher Site | Google Scholar
X. Hu and K. Duan, “Size effect and quasi-brittle fracture: the role of FPZ,” International Journal of Fracture, vol. 154, no. 1-2, pp. 3–14, 2008.
View at: Publisher Site | Google Scholar
J. Glucklich and L. J. Cohen, “Size as a factor in the brittle-ductile transition and the strength of some materials,” International Journal of Fracture Mechanics, vol. 3, no. 4, pp. 278–289, 1967.
View at: Publisher Site | Google Scholar
A. V. Dyskin, M. R. A. van Vliet, and J. G. M. van Mier, “Size effect in tensile strength caused by stress fluctuations,” International Journal of Fracture, vol. 108, no. 1, pp. 43–61, 2001.
View at: Publisher Site | Google Scholar
B. L. Karihaloo, H. M. Abdalla, and Q. Z. Xiao, “Deterministic size effect in the strength of cracked concrete structures,” Cement and Concrete Research, vol. 36, no. 1, pp. 171–188, 2006.
View at: Publisher Site | Google Scholar
J. Xu and X. He, “Size effect on the strength of a concrete member,” Engineering Fracture Mechanics, vol. 35, no. 4-5, pp. 687–695, 1990.
View at: Google Scholar
CEB-FIP Model Code 1990, Thomas Telford Ltd, Lausanne, Switerland, 1993.
K. Rokugo, Y. Uchida, H. Katoh, and W. Koyanagi, “Fracture mechanics approach to evaluation of flexural strength of concrete,” ACI Materials Journal, vol. 92, pp. 561–566, 1995.
View at: Google Scholar
J. K. Kim and S. H. Eo, “Size effect in concrete specimens with dissmiliar initial cracks,” Magazine of Concrete Research, vol. 42, pp. 233–238, 1990.
View at: Google Scholar
B. L. Karihaloo, H. M. Abdalla, and Q. Z. Xiao, “Size effect in concrete beams,” Engineering Fracture Mechanics, vol. 70, no. 7-8, pp. 979–993, 2003.
View at: Publisher Site | Google Scholar
V. Bindiganavile and N. Banthia, “Size effects and the dynamic response of plain concrete,” Journal of Materials in Civil Engineering, vol. 18, no. 4, pp. 485–491, 2006.
View at: Publisher Site | Google Scholar
J. Mazars, “A description of micro- and macroscale damage of concrete structures,” Engineering Fracture Mechanics, vol. 25, no. 5-6, pp. 729–737, 1986.
View at: Google Scholar
J. Mazars and G. Pijaudier-Cabot, “Continuum damage theory—application to concrete,” Journal of Engineering Mechanics, vol. 115, no. 2, pp. 345–365, 1989.
View at: Google Scholar
L. Peng, F. Liu, J. Ni, and X. Lai, “Size effects in thin sheet metal forming and its elastic-plastic constitutive model,” Materials and Design, vol. 28, no. 5, pp. 1731–1736, 2007.
View at: Publisher Site | Google Scholar
Z.-L. Wang, Y.-S. Liu, and R. F. Shen, “Stress-strain relationship of steel fiber-reinforced concrete under dynamic compression,” Construction and Building Materials, vol. 22, no. 5, pp. 811–819, 2008.
View at: Publisher Site | Google Scholar
Q. Li, C. Zhang, and G. Wang, “Dynamic damage constitutive model of concrete in uniaxial tension,” Engineering Fracture Mechanics, vol. 53, no. 3, pp. 449–455, 1996.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2014 Jikai Zhou et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

3635

Downloads

1149

Citations