Ambient Zinc K-Edge Extended X-Ray Absorption Fine Structure Studies on Solid Solution Hardening of the Ternary Alloys
Figure 5
Absorption oscillatory variations [χ()] for first shell contributions from Zn K-edge EXAFS absorption data are plotted in k-space for Zn1−xBexSe samples of composition (x) values of 0.0, 0.06, 0.16, 0.27, 0.33, and 0.42. The oscillations are extracted by using the window filter on the magnitude of the positively enveloped amplitude function A(r) as shown before in Figure 4(c) with the help of a dotted box type window, that is followed by the back FT.