Preparation and Properties of Biodegradable Film Composites Using Modified Cellulose Fibre-Reinforced with PVA

Table 3

Typical tensile properties of ten film composites.
S. no.Modified cellulose + PVATensile strength (MPa)Young's modulus (MPa)Elongation at break (mm)
1 1 0 + 9 0 18.36762469720.7569263275.7665531
2 2 0 + 8 0 19.00359353742.0972147274.9712453
3 3 0 + 7 0 19.56798685759.4714069272.1867043
4 4 0 + 6 0 19.62478011789.8828692249.2695623
5 5 0 + 5 0 19.9713187807.5349963218.3305132
6 6 0 + 4 0 20.12305195851.600451688.56065012
7 7 0 + 3 0 20.54942511875.453620471.98740953
8 8 0 + 2 0 21.16421162893.873660770.35176481
9 9 0 + 1 0 21.233819011093.20064858.0436579
10 9 5 + 0 5 22.415616821316.18587141.07783552