Research Article
Validation of FeSiMg Alloy Production Model for the Experimental Process
Table 1
Materials balance of the experimental heats.
| Heat no. | Input, gm | Output | Predicted Mg mass content in % | Dolomite | FeSi | Fluorspar | Limestone | Al | Quartzite | Bauxite | CeSo4 | Metal mass | Mg mass content in %, |
| 1 | 1250 | 750 | 100 | 50 | | | | 25 | 725 | 2.25 | 4.38 | 2 | 1250 | 750 | 100 | 70 | | | | 25 | 590 | 2.86 | 5.30 | 3 | 1250 | 750 | 100 | 100 | | | | 25 | 550 | 4.1 | 5.54 | 4 | 1250 | 750 | 100 | 130 | | | | 25 | 430 | 2.0 | 6.90 | 5 | 1250 | 750 | 100 | 150 | | | | 25 | 441.5 | 1.3 | 6.61 | 6 | 1250 | 600 | 160 | | 50 | 50 | | 25 | 480 | 1.7 | 5.48 | 7 | 1250 | 600 | 160 | | 50 | 75 | | 25 | 558 | 1.8 | 4.60 | 8 | 1250 | 600 | 160 | | 50 | 100 | | 25 | 622 | 3.2 | 4.04 | 9 | 1250 | 600 | 160 | | 50 | 150 | | 25 | 813 | 1.6 | 2.96 | 10 | 1250 | 600 | 40 | | 50 | | | 25 | 750 | 1.76 | 4.11 | 11 | 1250 | 600 | 80 | | 50 | | | 25 | 489 | 3.5 | 6.06 | 12 | 1250 | 600 | 120 | | 50 | | | 25 | 550 | 3.5 | 5.19 | 13 | 1250 | 600 | 160 | | 50 | | | 25 | 575 | 4.24 | 4.78 | 14 | 1250 | 600 | 200 | | 50 | | | 25 | 595 | 3.25 | 4.45 | 15 | 1250 | 600 | 400 | | 50 | | | 25 | 550 | 3.25 | 4.05 | 16 | 1250 | 950 | 160 | | | | 50 | 25 | 983 | 2.45 | 3.19 | 17 | 1250 | 950 | 160 | | | | 100 | 25 | 828 | 2.84 | 3.67 | 18 | 1250 | 950 | 160 | | | | 150 | 25 | 731 | 3.05 | 3.99 | 19 | 1250 | 950 | 160 | | | | 200 | 25 | 805 | 2.52 | 3.50 | 20 | 1250 | 950 | 160 | | | | 250 | 25 | 750 | 2.63 | 3.62 |
|
|