Abstract
The modelling of an axisymmetric industrial quenched chromium steel bar AISI-SAE 8650H based on finite element method has been produced to investigate the impact of process history on metallurgical and material properties. Mathematical modelling of 1-dimensional line (radius) element axisymmetric model has been adopted to predict temperature history and consequently the hardness of the quenched steel bar at any point (node). The lowest hardness point (LHP) is determined. In this paper hardness in specimen points was calculated by the conversion of calculated characteristic cooling time for phase transformation t8/5 to hardness. The model can be employed as a guideline to design cooling approach to achieve desired microstructure and mechanical properties such as hardness. The developed mathematical model is converted to a computer program. This program can be used independently or incorporated into a temperature history calculator to continuously calculate and display temperature history of the industrial quenched steel bar and thereby calculate LHP. The developed program from the mathematical model has been verified and validated by comparing its hardness results with commercial finite element software results.
1. Introduction
Quenching is a heat treatment usually employed in industrial processes in order to control mechanical properties of steels such as hardness [1]. The process consists of raising the steel temperature above a certain critical value, holding it at that temperature for a specified time and then rapidly cooling it in a suitable medium to room temperature [2]. The resulting microstructures formed from quenching (ferrite, cementite, pearlite, upper bainite, lower bainite, and martensite) depend on cooling rate and on chemical composition of the steel [3].
Quenching of steels is a multiphysics process involving a complicated pattern of couplings among heat transfer, because of the complexity, coupled (thermal-mechanical-metallurgical) theory, and nonlinear nature of the problem, no analytical solution exists; however, numerical solution is possible by finite difference method, finite volume method, and the most popular one-finite element method (FEM) [4]. During the quenching process of the steel bar, the heat transfer is in an unsteady state as there is a variation of temperature with time [5]. The heat transfer analysis in this paper will be carried out in 3-dimensions. The three dimensional analysis will be reduced into a 1-dimensional axisymmetric analysis to save cost and computer time [4, 6, 16]. This is achievable because in axisymmetric conditions, there is no temperature variation in the theta () direction and in (z) direction, the temperature deviations are only in (r). The Galerkin weighted residual technique is used to derive the mathematical model. In this paper, 1-dimensional line (radius) element will be developed.
2. Mathematical Model
The temperature history of the quenched cylindrical steel bar at any point would be calculated; three-dimensional heat transfer can be analyzed using one dimensional axisymmetric elements as shown in Figures 1, 2, and 3.
The linear temperature distribution for an element (radius) line, is given by: where = nodal temperature as the function of , and are constants, is any point on the (radius) line element.
2.1. Shape Function of the Axisymmetric Triangular Element
The shape functions were to represent the variation of the field variable over the element. The shape function of axisymmetric 1-dimensional line (radius) element expressed in terms of the coordinate and its coordinate as shown in Figure 4; which are derived to obtain the following shape functions as shown: Thus the temperature distribution of 1D radius for an element in terms of the shape function can be written as: where [S(r)] = is a row vector matrix and is a column vector of nodal temperature of the element.
Equation (3) can also be expressed in matrix form as: Thus for 1-dimensional element we can write in general: where and represent the nodal values of the unknown variable such as in our case temperature also the unknown can be deflection, velocity, and so forth.
2.2. Natural Area Coordinate
Using the natural length coordinates and their relationship with the shape function by simplification of the integral of Galerkin solution.
The two length natural coordinates and at any point P inside the element are shown in Figure 5 from which we can write: Since it is a one-dimensional element, there should be only one independent coordinate to define any point P. This is true even with natural coordinates as the two natural coordinates and are not independent, but are related as: The natural coordinates and are also the shape functions for the line element, thus:
2.3. Develop Equation for All Elements of the Domain
Derivation of equation of heat transfer in axisymmetric one-dimensional line (radius) elements by pplying the conservation of energy to a differential volume cylindrical segment as shown in Figure 6, The transient heat transfer within the component during quenching can mathematically be described by simplifying the differential volume term; the heat conduction equation is derived and given by = heat conductivity coefficient in r-direction, W/m°C, = heat conductivity coefficient in θ-direction, W/m°C, = heat conductivity coefficient in z-direction, W/m°C, = temperature, °C, = heat generation, W/m3, = mass density, kg/m3, c = specific heat of the medium, J/kgK, t = time, s.
The assumptions made in this problem were:
(i) for axisymmetric situations one dimensional line (radius) element, there is no variation of temperature in the Z-direction as shown in Figures 1, 2, and 3. Because we already assumed that in steel quenching and cooling process of the steel bar is insulated from convection at the cross section of the front and back.
It means that we have convection and radiation at one node only which is on the surface (node 5), in our research we focus to calculate LHP which is at (node 1), where it is the last point will be cooled, this give the maximum advantage to make our assumption more safe, because it is the last point which will effect by convection and radiation from the front and back cross-section of the steel bar therefore we can write, ,
(ii) for axisymmetric situations, there is no variation of temperature in the -direction, because it is clear from Figures 1, 2, and 3 that the temperature distribution along the radius will be the same if the radius move with angle θ, 360° therefore, ,
(iii) the thermal energy generation rate represent the rate of the conversion of energy from electrical, chemical, nuclear, or electromagnetic forms to thermal energy within the volume of the system. Such as conversion is the electric field which will be studied with details in the 2nd part of our research, however in this manuscript no heat generation therefore, After simplifying, (11) becomes and also known as residual or partial differential equation
2.4. Galerkin Weighted Residual Method Formulation
From the derived heat conduction equation, the Galerkin residual for 1-dimensional line (radius) element in an unsteady state heat transfer by integration the shape functions times the residual which minimize the residual to zero becomes where = the transpose of the shape function matrix, = the residual contributed by element to the final system of equations
2.5. Chain Rule
The terms 1 and 2 of (16) can be rearranged using the chain rule which states that; Therefore, , Term 1 of (16) is rearranged, thus By substituting (19) in to (16), get Term is the heat convection terms and contributes to the conductance and thermal load matrix. Term is the heat conduction terms and contributes to the conductance matrix. Term is the transient equation and contributes to the capacitance matrix, where Note that term and term contributed to the conductance matrix since they contains the unknown temperature . Terms and contributed to the thermal load matrix as is the known fluid temperature. Term and term heat radiation are very important if our heat treatment is annealing (cooling in the furnace) or normalizing (cooling in air or jet air), but can be ignore (neglect) if the cooling is quenching in water as in our paper.
From earlier explanations, derivation and after simplifying we can formulate the conductance matrix in the -direction for Term finally we get:
Term B (the conduction term) contributes to the conductance matrix: Similarly, Term is the unsteady state (transient) which contributes to the Capacitance Matrix,
Term C (heat stored) contributes to the Capacitance Matrix:
Term A (heat convection): (i)Term : contributes to conductance matrix,
Term (the convection term) contributes to the conductance matrix:(ii)Term : contributes to thermal load Matrix:
Term (the convection term) contributes to thermal load matrix
2.6. Construct the Element Matrices to the Global Matrix
Assemble the global, conductance, capacitance, and thermal load matrices and the global of the unknown temperature matrix for all the elements in the domain, that is, the element’s conductance, capacitance and thermal load matrices have been derived. Assembling these elements is necessary in all finite element analysis.
Constructing these elements will result into the following finite element equation: with . Conductance matrix due to conduction (elements 1 to 4) and heat loss through convection at the element’s boundary (element 4 node 5) as shown in Figures 1 and 2:: Temperature value at each node, °C,: Capacitance matrix, due to transient equation (heat stored),: Temperature rate for each node, °C/s,: heat load due to heat loss through convection at the element’s boundary (element 4 node 5) and internal heat generation (element 4 node 5).
2.7. Euler’s Method
Two point recurrence formulas will allow us to compute the nodal temperatures as a function of time. In this paper, Euler’s method which known as the backward difference scheme (BDS) will be used to determine the rate of change in temperature, the temperature history at any point (node) of the steel bar [3].
If the derivative of T with respect to time t is written in the backward direction and if the time step is not equal to zero , we have that, with = temperature rate (°C/s); = temperature at s(°C); = temperature at s, (°C) = selected time step (s) and t = time (s) (at starting time, = 0).
By substituting the value of into the finite element global equation, we have that Finally, the matrices become From (29) all the right hand side is completely known at time , including for which the initial condition apply.
Therefore, the nodal temperature can be obtained for a subsequent time given the temperature for the preceding time.
Once the temperature history is known the important mechanical properties of the steel bar can be obtained such as hardness and strength.
3. Application
3.1. Calculation the Temperature History
The present developed mathematical model is programmed using MATLAB to simulate the results of the temperature distribution with respect to time in transient state heat transfer of the industrial quenched steel bar. The cylindrical chromium steel bar has been heated to 850°C. Then being quenched in water with = 32°C, the water convection heat transfer coefficient, = 5000 W/m2°C.
The temperature history at any point (node) of the cylindrical steel bar after quenched is being identified in Figures 6 and 7. The cylindrical bar was made from chromium steel 8650H, with properties as mentioned below.
Thermal capacity, (J/m3·°C):°C, ,°C, ,°C, ,°C, .
Thermal conductivity, k (W/m°C)°C, ,°C, ,
where in our case the global conductance matrix , the global capacitance matrix and the global thermal load matrix can be computed easily as the following: where , , , are the conductance matrices due to conduction in 1-dimensional element for the 1st element, the 2nd, the 3rd, and the 4th element respectively while because we note that there is convection in element 4 at node only as shown clearly in Figures 3 and 7: where , , , are the capacitance matrices due to transient [unsteady state] in 1-dimensional line (radius) element:
We have convection in element 4 at node only as shown clearly in Figures 3 and 7.
With the input data and boundary conditions provided, a sensitivity analysis is carried out with the developed program to obtain the temperature distribution at any point (node) of the quenched steel bar, as example, is the transient state temperature distribution results of the selected five nodes from the center to the surface of the quenched steed bar which were computed as shown in Figures 7 and 8.
3.2. LHP Calculation
3.2.1. Calculating the Cooling Time Required
In this study, we choose to calculate the cooling time between 800°C and 500°C [3, 7–9], where the characteristic cooling time, relevant for phase transformation in most structural steels is the time of cooling from 800 to 500°C (time ) [10–17]: From Figure 7 we can determine the time taken for node to reach 800°C, By the same way the time taken for node to reach 500°C is sec.
So the Cooling time for node ;
For nodes to , the cooling time calculated by the same way, the final results shown in Table 1.
Table 1 shows the cooling time and the rate of cooling ROC.
3.2.2. Calculating the Jominy Distance from Standard Jominy Distance versus Cooling Time Curve
Cooling time, , obtained will now be substituted into the Jominy distance versus cooling time curve to get the correspondent Jominy distance. Jominy distance can also be calculated by using polynomial expressions via polynomial regression via Microsoft Excel.
The standard Table (cooling rate at each Jominy distance (Chandler, 1999)) can be used too [18].
Then Jominy distance of nodes to will be calculated, the final results shown in Table 2, where the rate of cooling, ROC, was defined by;
3.2.3. Predict the Hardness of the Quenched Steel Bar
The HRC of AISI-SAE 8650H can be calculated by using the relation between the J-Distance and the HRC from the Practical date Handbook, the Timken Company 1835 Duebex Avenue SW Canton, Ohio 44706-2798 1-800-223, the final results are shown in Figure 9 and Table 3.
4. Mathematical Model Verification
The same data input for the steel properties and boundary condition used in the mathematical model is applied to the ANSYS software to verify the temperature simulation results. The temperature distribution from the ANSYS analysis is depicted figuratively as shown in Figures 10(a) and 10(b).
(a)
(b)
The temperature time graph from the ANSYS analysis is depicted as shown in Figure 11.
From the graphs shown in Figure 8 by mathematical model and Figure 11 by ANSYS, it can be clearly seen that the temperature history of the quenched steel bar have the same pattern. The heat transfer across the steel bar is uniform. From Figure 11 the cooling time, Jominy-distance, and consequently the hardness of the quenched chromium steel bar at any point (node), even the lowest hardness point (LHP) is determined by ANSYS too, the final results shown in Table 4 and Figure 12.
From our results we found that in the mathematical model for the 1st node with in the center, we found that HRC = 59.297. While in ANSYS for the same node , we found that HRC = 58.492.
And for the nodes on the surfaces and , it was found that HRC = 61.421 and 61.295 for the mathematical model and ANSYS, respectively. From the above, it can be seen that there is a strong agreement between both results. The difference between all the results of the mathematical model and the ANSYS simulations can be accounted due to the fact that the ANSYS software is commercial purpose, and thereby has some automated input data. But the developed mathematical model is precisely for a circular steel bar axisymmetric cross section. However, there is strong agreement between both results and thereby the result is validated, where the comparison indicated reliability of the proposed model.
Also the results showed that the node on the surface will be the 1st which completely cooled after quenching because it is in the contact with the cooling medium then the other nodes on the radial axis to the centre, respectively, and the last point will be completely cooled after quenching will be at half the length at the centre. Hence LHP will be at half the length at the centre of the quenched industrial chromium steel bar. It will be more important to know LHP once the radius of the quenched steel bar is large because LHP will be low, in other words, it will be lower than the hardness on the surface, that means increasing the radius of the bar inversely proportional with LHP.
LHP calculation experimentally is an almost impossible task using manual calculation techniques also the earlier methods only used hardness calculated at the surface, which is higher than LHP, which has negative consequence that can result to the deformation and failure of the component.
5. Conclusion
A mathematical model of steel quenching has been developed to compute LHP of the quenched chromium steel bar at any point (node) in a specimen with cylindrical geometry. The model is based on the finite element Galerkin residual method. The numerical simulation of quenching consisted of numerical simulation of temperature transient field of cooling process. This mathematical model was verified and validated by comparing the hardness results with ANSYS software simulations. From the mathematical model and ANSYS results, it is clear that the nodes on the surface ( and ), respectively, cools faster than the nodes on the center ( and ) because and , this means that the mechanical properties will be different such as hardness where the hardness on the surface nodes ( and ) will be higher than the hardness on the center nodes ( and ).
Acknowledgments
The authors would like to thank the University Tun Hussein Onn Malaysia for supporting this research under the Science Fund Grant. The corresponding author grateful to the Postgraduate Centre of UTHM for their support of this research, where they accepted him under the university Ph.D. scholarship.