Aqueous Photo-Living Radical Polymerization of Sodium Methacrylate Using a Water-Soluble Nitroxide Mediator
Table 1
The photopolymerization of NaMA in water.
| Run no. | V-80 (mM) | HTEMPO (mM) | FS (mM) | Time (h) | Conversion (%) | Mn
a | Mw/Mn
a |
| 1 | — | — | — | 1 | 98 | 208,000 | 29.36 | 2 | 44.8 | — | — | 1 | 100 | 86,800 | 10.66 | 3 | — | — | 25.3 | 1 | 95 | 202,000 | 46.27 | 4 | 44.8 | — | 25.3 | 1 | 98 | 93,800 | 15.04 | 5 | 44.8 | 47.6 | — | 6 | 61 | 101,000 | 3.19 | 6 | — | 47.6 | 25.3 | 5 | 53 | 52,500 | 2.36 | 7 | 44.8 | 47.6 | 25.3 | 9 | 78 | 60,400 | 2.05 | 8 | 44.8 | 95.2 | 25.3 | 5 | 0 | — | — | 9 | 44.8 | 47.6 | 50.6 | 5 | 55 | 65,700 | 2.58 | 10 | 8.96 | 9.52 | 5.06 | 20 | 92b | 20,300 | 3.71 |
|
|
[NaMA]0 = 9.25 mM.
aEstimated by GPC based on PNaMA standards.
b[NaMA]0 = 1.85 mM.
|