Experimental Study of the Interaction between Recrystallization and Precipitation Processes of an AA8011 Commercial Alloy
Figure 2
(a) Thermoelectric power and (b) derivative of the thermoelectric power versus temperature for the homogenized AA8011 alloy, quenched and deformed at different rolling degrees, then annealed continuously at 2°C/min.