Effect of Crystallinity of β- and βbc-Nickel Hydroxide Samples on Chemical Cycling
Table 3
Estimation of lattice strain of as-prepared, oxidized, and reduced phases of β-nickel hydroxide and βbc-nickel hydroxide samples.
| hkl | β-nickel hydroxide | βbc-nickel hydroxide | Lattice strain | Lattice strain | As prepared | β-nickel hydroxide oxidised phase | β-nickel hydroxide oxidised phase reduction using H2O2 | As prepared | βbc-nickel hydroxide oxidised phase using NaClO | βbc-nickel hydroxide oxidised phase using NaClO followed by reduction using H2O2 | β (Cos θ/λ) × 10−3 | (Sin θ/λ) | β (Cos θ/λ) × 10−3 | (Sin θ/λ) | β (Cos θ/λ) × 10−3 | (Sin θ/λ) | β (Cos θ/λ) | (Sin θ/λ) | β (Cos θ/λ) × 10−3 | (Sin θ/λ) | β (Cos θ/λ) | (Sin θ/λ) |
| 001 | 1.49 | 0.1083 | 2.48 | 0.1041 | 3.145 | 0.1078 | 0.03769 | 0.107 | 0.0261 | 0.1073 | 0.04727 | 0.1089 | 100 | 4.55 | 0.1844 | — | | 1.45 | 0.1842 | 7.13 × 10−3 | 0.1854 | 0.0678 | 0.2119 | 4.346 × 10−3 | 0.1852 | 101 | 1.47 | 0.2139 | 8.44 | 0.2136 | 2.841 | 0.2135 | 0.0255 | 0.214 | — | | 0.0239 | 0.2139 | 102 | 2.46 | 0.2841 | — | | 3.589 | 0.2842 | 0.0369 | 0.283 | — | | 0.0298 | 0.2844 | 110 | 1.161 | 0.3194 | — | | 2.57 | 0.3192 | 7.122 × 10−3 | 0.320 | 0.04109 | 0.3299 | 3.762 × 10−3 | 0.32 | 111 | 2.51 | 0.3374 | — | | 4.08 | 0.337 | 0.01512 | 0.337 | — | | 0.32 | 0.3369 |
|
|