Effect of Pharmaceutically Active Compound Nitroxoline on the Corrosion of Mild Steel in an Acidic Environment
Table 4
AC impedance spectroscopy parameters for mild steel corrosion in 1 M sulphuric acid solution at various concentrations of the inhibitor.
| Nitroxoline conc. (ppm) | (cm2) | (cm2) | (μF cm−2) | Surface coverage (θ) | IE (%) η |
| H2SO4 (blank) | 5.303 | 10.636 | 2823.2 | — | — | 50 | 16.004 | 32.033 | 310.61 | 0.6680 | 66.80 | 100 | 18.298 | 36.712 | 237.04 | 0.7103 | 71.03 | 150 | 20.058 | 40.180 | 197.58 | 0.7353 | 73.53 | 200 | 22.184 | 44.474 | 161.40 | 0.7608 | 76.08 | 250 | 26.105 | 52.588 | 115.99 | 0.7977 | 79.77 | 300 | 35.152 | 70.499 | 64.26 | 0.8491 | 84.91 |
|
|