Inhibition of Aluminium Corrosion in 1.0 M HCl by Caffeine: Experimental and DFT Studies
Table 2
Parameters of the Dubinin-Radushkevich model.
| (K) | | (kJ−2 mol2) | | (kJ mol−1) |
| 303 | 0.991 | 0.0121 | 0.696 | 6.4 | 308 | 0.995 | 0.0081 | 0.582 | 7.9 | 313 | 0.984 | 0.0063 | 0.517 | 8.9 | 318 | 0.965 | 0.0063 | 0.466 | 8.9 | 323 | 0.974 | 0.0061 | 0.401 | 9.0 |
|
|