On the Issue of Radiation-Induced Instability in Binary Solid Solutions

Figure 1

Stable (𝜔₁…𝜔₅) and unstable (𝜔₆) growth factors (eigenvalues) of the system calculated at temperature 850 K and a dpa rate of 2 × 10⁻⁶ dpa/𝑡̃. The fractional alloy concentration is 𝐶_Cu=0.1 and 𝐶_Au=0.9.