Effect of Dilution on Microstructure and Wear Resistance of a Fe-Based Hardfacing Alloy with a High Amount of Carbide-Forming Elements
Figure 6
Primary phase evolution with increasing dilution rate (a), fraction of the M7C3 carbides, M2B borides, and Mo-rich phases in the diluted alloys (b).