Effect of Dilution on Microstructure and Wear Resistance of a Fe-Based Hardfacing Alloy with a High Amount of Carbide-Forming Elements
Table 1
Composition (mass %) of the base alloy and diluted alloys.
| ā | C + B | Ni | Mn | Cr | Si | V | Mo | Cu | Fe |
| Base alloy | 5.72 | 4.46 | 0.50 | 9.7 | 2.04 | 0.09 | 5.29 | 1.20 | Bal. | Base alloy + 20Fe | 4.59 | 3.20 | 0.22 | 7.61 | 1.66 | 0.08 | 4.30 | 1.19 | Bal. | Base alloy + 30Fe | 4.02 | 2.80 | 0.19 | 6.66 | 1.46 | 0.07 | 3.76 | 1.04 | Bal. | Base alloy + 40Fe | 3.44 | 2.40 | 0.16 | 5.71 | 1.25 | 0.06 | 3.22 | 0.89 | Bal. | Base alloy + 50Fe | 2.87 | 2.00 | 0.14 | 4.76 | 1.04 | 0.05 | 2.69 | 0.75 | Bal. |
|
|