Effect of Dilution on Microstructure and Wear Resistance of a Fe-Based Hardfacing Alloy with a High Amount of Carbide-Forming Elements

<table class="table-group" id="tab2"><tr><td><table class="table"><tr><td class="thead-hr" colspan="2"><hr/></td></tr><tr class="thead"><td align="left">Alloy</td><td align="center">Volume loss (<svg height="9.4034pt" id="M8" style="vertical-align:-3.40335pt" version="1.1" viewbox="-0.0498162 -6.00005 7.4591 9.4034" width="7.4591pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M546 97L529 123C499 91 459 65 450 65C443 65 439 73 445 106C468 226 496 341 523 451H513L436 424C423 357 412 311 403 276C356 195 245 59 190 59C165 59 158 99 166 135L236 445L227 451L152 428L60 18C43 -58 24 -145 24 -183C24 -237 43 -257 66 -257C96 -257 123 -236 130 -224L129 -216C115 -205 96 -156 96 -102C96 -57 105 -7 113 26H115C127 -1 137 -12 158 -12S198 -5 230 19C284 60 332 117 385 186H387C381 154 378 142 370 107C347 1 367 -12 388 -12C422 -12 492 32 546 97Z" id="g50-234"></path><glyph.data ascent="3443" descent="-2856" horiz-adv-x="564" vert-adv-y="564"></glyph.data></g></svg>m<sup>3</sup>)</td></tr><tr><td class="thead-hr" colspan="2"><hr/></td></tr><tr><td align="left">Base alloy</td><td align="center">384 × 10<sup>4</sup>  ± 44.7</td></tr><tr><td align="left">Base alloy + 30Fe</td><td align="center">1193 × 10<sup>4</sup>  ± 70.3</td></tr><tr class="table-tr"><td colspan="2"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

Volume loss of the investigated alloys after wear tests.

Conference Papers in Science

tab2

Table 2

Table 2: Effect of Dilution on Microstructure and Wear Resistance of a Fe-Based Hardfacing Alloy with a High Amount of Carbide-Forming Elements 