A Numerical Formula for General Prediction of Interface Bonding between Alumina and Aluminum-Containing Alloys

Table 2

Values of oxide formation enthalpy and calculated adsorption energy of oxygen on various metals (M) and related values.

kJ/molkJ/mol-MkJ/mol-OkJ/mol-OEnergy difference (kJ/mol)

MgMgO601.6601.6601.6664.14 419.61
AlAl2O31675.7837.85558.5667833.06 588.53
SiSiO2910.7910.7455.35885.15 640.62
TiTiO2944944472908.96 664.43
VV2O51550.6775.3310.12788.34 543.81
CrCr2O31139.7569.85379.9641.44 396.91
MnMnO2520520260605.80 361.27
FeFe2O3824.2412.1274.7333528.65 284.12
CO CO3O4891297222.75446.36 201.83
NiNi2O3489.5244.75163.1667409.00 164.47
CuCuO157.3157.3157.3346.47 101.94
ZnZnO350.5350.5350.5484.61 240.08
GaGa2O31089.1544.55363.0333623.35 378.82
GeGeO2580580290648.70 404.17
ZrZrO21094.3 1094.324 547.162 1016.44 771.91
NbNb2O51899.5949.75379.9913.07 668.54
MoMoO3745.1745.1248.3667766.75 522.22
RuRuO4239.3239.359.825405.10 160.57
RhRh2O3343.0 171.5114.3333356.62 112.09
PdPdO85.485.485.4295.06 50.53
AgAg2O224.312.1512.15242.69 −1.84
InIn2O3925.8462.9308.6564.97 320.44
SnSnO2577.63577.63288.815647.01 402.48
LaLa2O31793.7896.85597.9875.25 630.72
HfHfO21144.71144.7572.351052.46 807.93
TaTa2O520461023409.2965.45 720.92
WWO3842.9842.9280.9667836.67 592.14
ReRe2O71240.1620.05177.1571677.34 432.81
OsOsO4391.248 391.248 97.812 513.74 269.21
IrIrO2274.1274.1137.05429.98 185.45
PtPtO2133.3133.366.65329.31 84.78
Au<0<0<0<0<0
HgHgO90.7990.7990.79298.91 54.38
PbPbO218218218389.87 145.34
BiBi2O3573.9191.3286.95370.78 126.25