Hot Corrosion Behaviour of Detonation Gun Sprayed
Al2O3-40TiO2 Coating on Nickel Based Superalloys at 900°C
Figure 2
Weight gain/area versus number of cycles plot for Al2O3-40TiO2 coated and bare superalloys subjected to Na2SO4-82%Fe2(SO4)3 at 900°C for 50 cycles.