Hot Corrosion Behaviour of Detonation Gun Sprayed Al
2
O
3
-40TiO
2
Coating on Nickel Based Superalloys at 900°C
Table 1
Chemical compositions of Superni 718 and AE 435 superalloys Midhani grade chemical composition (wt.%).
Materials
C
Mn
Si
S
P
Cu
Cr
Fe
Ti
Al
Ni
Superni 718
0.0047
0.01
0.02
0.002
—
0.010
17.78
19.56
—
—
Bal
AE 435
0.08
0.03
0.03
>0.005
>0.005
>0.01
20.19
0.10
0.30
0.12
Bal