Hot Corrosion Behaviour of Detonation Gun Sprayed Al
2
O
3
-40TiO
2
Coating on Nickel Based Superalloys at 900°C
Table 4
Parabolic rate constant (
) for the Al
2
O
3
-40TiO
2
coated and uncoated Superni 718 and AE 435 superalloys.
Substrate
Values (×10
−10
g
2
cm
−4
s
−1
)
Superni 718
66.376
Coated Superni 718
39.443
AE 435
28.995
Coated AE 435
6.7245