Mechanical Characterization and Machinability Behavior of Annealed AISI D6 Cold Working Steel
Table 5
Matrix design and experimental data.
| Std. | Run | (m/min) | “” (mm) | “” (mm) | (degree) | (μm) | (N) |
| 3 | 1 | 39.6 | 0.27 | 0.2 | 45 | 2.78 | 349 | 2 | 2 | 97.5 | 0.10 | 0.2 | 45 | 0.76 | 164 | 13 | 3 | 39.6 | 0.10 | 1.0 | 90 | 4.18 | 461 | 11 | 4 | 39.6 | 0.27 | 0.2 | 90 | 3.35 | 170 | 4 | 5 | 97.5 | 0.27 | 0.2 | 45 | 3.22 | 298 | 6 | 6 | 97.5 | 0.10 | 1.0 | 45 | 2.76 | 412 | 1 | 7 | 39.6 | 0.10 | 0.2 | 45 | 0.96 | 188 | 15 | 8 | 39.6 | 0.27 | 1.0 | 90 | 4.09 | 871 | 10 | 9 | 97.5 | 0.10 | 0.2 | 90 | 0.71 | 108 | 14 | 10 | 97.5 | 0.10 | 1.0 | 90 | 4.91 | 408 | 7 | 11 | 39.6 | 0.27 | 1.0 | 45 | 3.08 | 614 | 12 | 12 | 97.5 | 0.27 | 0.2 | 90 | 2.90 | 189 | 5 | 13 | 39.6 | 0.10 | 1.0 | 45 | 3.28 | 307 | 8 | 14 | 97.5 | 0.27 | 1.0 | 45 | 1.07 | 722 | 9 | 15 | 39.6 | 0.10 | 0.2 | 90 | 1.06 | 132 | 16 | 16 | 97.5 | 0.27 | 1.0 | 90 | 3.11 | 747 |
|
|