Oxidation/Corrosion Behaviour of ODS Ferritic/Martensitic Steels in Pb Melt at Elevated Temperature
Figure 4
Morphology and elemental amount of scales formed on ODS Fe-14Cr steel after exposure to static oxygen-saturated Pb-melt at 550°C for 500 h.