Raman Spectroscopy and Statistical Analysis of the Silicate Species and Group Connectivity in Cesium Silicate Glass Forming System
Table 1
The peak positions (cm
−1), relative intensities, and fractions of
species (%) in investigated glasses and melts.
| , K | H1 (H1) | H2 (H2) | H3 | H4 | H5 | H6 | | | |
| 17%Cs2O-83%SiO2 | 293 | 1008/0.020 | 1060/0.072 | 1098/0.325 | 1144/0.583 | — | — | 59 | 41 | — |
| 22%Cs2O-78%SiO2 | 293 | 1010/0.020 | 1065/0.068 | 1100/0.352 | 1145/0.560 | — | — | 44 | 56 | — | 473 | 1007/0.021 | 1063/0.074 | 1099/0.328 | 1142/0.577 | — | — | 44 | 56 | — | 683 | 1006/0.019 | 1060/0.074 | 1097/0.333 | 1140/0.574 | — | — | 44 | 56 | — | 793 | 1006/0.025 | 1060/0.081 | 1096/0.323 | 1138/0.571 | — | — | 44 | 56 | — | 898 | 1006/0.031 | 1059/0.093 | 1095/0.315 | 1135/0.555 | 935/0.006 | — | 46/45 | 52/54 | 2/1 | 1003 | 1004/0.035 | 1059/0.108 | 1095/0.308 | 1133/0.540 | 937/0.009 | — | 46/45 | 52/54 | 2/1 | 1113 | 1004/0.038 | 1056/0.128 | 1092/0.304 | 1129/0.517 | 931/0.013 | — | 46/45 | 51/53 | 3/2 | 1223 | 1001/0.049 | 1053/0.143 | 1091/0.285 | 1127/0.500 | 926/0.023 | — | 47/47 | 49/50 | 4/3 | 1443 | 998/0.062 | 1052/0.167 | 1091/0.259 | 1124/0.479 | 920/0.033 | — | 48/48 | 47/48 | 5/4 | 1553 | 998/0.067 | 1050/0.191 | 1088/0.249 | 1123/0.452 | 922/0.041 | — | 49/49 | 45/46 | 6/5 |
| 27%Cs2O-73%SiO2 | 293 | 1006/0.024 | 1062/0.105 | 1097/0.361 | 1139/0.505 | 929/0.005 | — | 28/27 | 70/73 | 2/<1 | 573 | 1005/0.022 | 1062/0.144 | 1097/0.354 | 1137/0.474 | 932/0.006 | — | 28/27 | 70/73 | 2/<1 | 683 | 1005/0.022 | 1062/0.134 | 1096/0.350 | 1135/0.490 | 935/0.004 | — | 28/27 | 70/73 | 2/<1 | 793 | 1005/0.024 | 1060/0.155 | 1094/0.344 | 1133/0.469 | 936/0.008 | — | 28/27 | 70/72 | 2/1 | 898 | 1002/0.024 | 1060/0.151 | 1094/0.340 | 1129/0.477 | 932/0.008 | — | 28/27 | 70/72 | 2/1 | 1003 | 1003/0.026 | 1058/0.158 | 1092/0.335 | 1127/0.471 | 929/0.010 | — | 29/27 | 69/71 | 2/2 | 1113 | 1002/0.036 | 1057/0.168 | 1093/0.324 | 1125/0.452 | 926/0.020 | — | 30/29 | 66/68 | 4/3 | 1223 | 1000/0.044 | 1055/0.188 | 1092/0.307 | 1122/0.433 | 923/0.028 | — | 31/30 | 64/66 | 5/4 | 1338 | 1001/0.051 | 1055/0.194 | 1090/0.285 | 1120/0.428 | 920/0.042 | — | 32/32 | 61/63 | 7/5 | 1553 | 1000/0.070 | 1052/0.209 | 1088/0.237 | 1119/0.426 | 916/0.058 | — | 34/34 | 57/58 | 9/8 |
| 33%Cs2O-67SiO2 | 293 | 1001/0.042 | 1060/0.177 | 1103/0.569 | 1143/0.184 | 934/0.028 | — | 7/6 | 87/89 | 7/6 | 573 | 996/0.043 | 1059/0.177 | 1101/0.566 | 1141/0.183 | 930/0.031 | — | 7/6 | 86/89 | 7/6 | 683 | 992/0.042 | 1058/0.179 | 1098/0.563 | 1137/0.184 | 927/0.032 | — | 7/6 | 86/89 | 7/6 | 793 | 989/0.046 | 1057/0.188 | 1096/0.539 | 1134/0.193 | 925/0.034 | — | 8/7 | 85/87 | 8/7 | 898 | 988/0.043 | 1056/0.185 | 1094/0.548 | 1130/0.191 | 922/0.033 | — | 7/6 | 86/88 | 7/6 | 1003 | 989/0.056 | 1057/0.240 | 1092/0.434 | 1128/0.225 | 918/0.045 | — | 9/8 | 82/84 | 9/8 | 1113 | 991/0.064 | 1056/0.233 | 1095/0.412 | 1130/0.238 | 917/0.053 | — | 11/10 | 79/81 | 11/10 | 1223 | 992/0.075 | 1057/0.240 | 1096/0.374 | 1130/0.245 | 918/0.066 | — | 13/12 | 75/76 | 13/12 | 1338 | 989/0.093 | 1054/0.258 | 1092/0.299 | 1126/0.262 | 916/0.088 | — | 15/15 | 69/70 | 15/15 | 1443 | 990/0.123 | 1057/0.266 | 1089/0.243 | 1123/0.275 | 915/0.093 | — | 18/18 | 64/64 | 18/18 |
| 37%Cs2O-63%SiO2 | 293 | 1005/0.088 | 1063/0.189 | 1099/0.579 | 1136/0.055 | 928/0.089 | — | <1 | 82/83 | 18/17 | 573 | 1006/0.089 | 1062/0.176 | 1099/0.586 | 1137/0.057 | 927/0.092 | — | <1 | 81/82 | 18/18 | 1003 | 1001/0.086 | 1060/0.186 | 1095/0.553 | 1134/0.083 | 922/0.083 | 871/0.009 | <1 | 82/83 | 18/17 | 1113 | 1004/0.113 | 1062/0.216 | 1092/0.439 | 1130/0.120 | 919/0.091 | 872/0.021 | 4/4 | 74/74 | 22/22 | 1223 | 998/0.117 | 1057/0.236 | 1089/0.409 | 1127/0.114 | 912/0.105 | 867/0.019 | 5/5 | 72/72 | 23/23 | 1338 | 994/0.125 | 1052/0.270 | 1085/0.344 | 1122/0.126 | 906/0.107 | 860/0.028 | 7/7 | 69/68 | 24/25 | 1443 | 991/0.134 | 1055/0.263 | 1086/0.308 | 1121/0.139 | 903/0.128 | 855/0.028 | 9/9 | 65/64 | 26/27 |
|
|