Tribological Behavior of Hastelloy C and Refractalloy 26

Department of Industrial Engineering II, University of A Coruña, C/Mendizábal s/n, 15403 Ferrol, Spain

Received 21 July 2011; Accepted 12 September 2011

Academic Editors: R. Brighenti and X. Yang

Copyright © 2011 A. Varela et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Linked References

  1. L. Yingjie, B. Xingui, and C. Keqiang, “A study on the formation of wear debris during abrasion,” Tribology International, vol. 18, no. 2, pp. 107–111, 1985. View at Google Scholar · View at Scopus
  2. H. Berns, A. Fischer, and S. D. Franco, Congresso Anual Associacao Brasileira de Metalurgia e Materiais, 1995.
  3. X. Xu, Y. Yu, and H. Huang, “Mechanisms of abrasive wear in the grinding of titanium (TC4) and nickel (K417) alloys,” Wear, vol. 255, no. 7–12, pp. 1421–1426, 2003. View at Publisher · View at Google Scholar · View at Scopus
  4. B. Bouaifi and U. Draugelates, “Precipitation-hardenable nickel-based super alloys for wear resistance in the high-temperature range,” Materials and Corrosion, vol. 54, no. 12, pp. 988–994, 2003. View at Publisher · View at Google Scholar · View at Scopus
  5. U. Wende, B. Bouaifi, S. Bauer, and A. Bock, “Auftragschweißen mit ausscheidungshärtbaren Nickelbasis-Superlegierungen für den Verschleißschutz im Hochtemperaturbereich,” DVS-Berichte, vol. 220, pp. 84–93, 2002. View at Google Scholar
  6. “Standard test method for wear testing with a pin-on-disk apparatus,” in Annual Book of ASTM Standars, vol. 03.02 of ASTM G99-05, pp. 408–412, ASTM International, 2008.
  7. G. F. Vander Voort, Metallography: Principles and Practice, McGraw–Hill, 1984.
  8. K. Yang, S. Yu, Y. Li, and C. Li, “Effect of carbonitride precipitates on the abrasive wear behaviour of hardfacing alloy,” Applied Surface Science, vol. 254, no. 16, pp. 5023–5027, 2008. View at Publisher · View at Google Scholar · View at Scopus