Densification and Microstructural Evolutions during Reaction Sintering of SiC-Si-C Powder Compacts
Figure 2
Optical micrographs from SiC-Si-C ceramics at RS temperatures of (a) 1400, (b) 1500, and (c) 1600°C. Si powder content of 10 wt.%, Si/C ratio of 1, initial SiC particle size of 50 nm, and RS time of 2 h were used.