Densification and Microstructural Evolutions during Reaction Sintering of SiC-Si-C Powder Compacts

<table>XRD patterns of SiC-Si-C ceramics at different RS temperatures and times. Si powder content of 5 wt.%, Si/C ratio of 1 and initial SiC particle size of 50 nm were used.</table>