Secondary Relaxation inside the Glass
Table 3
Parameters of the thermodynamic paths used in this study to vitrify the systems; (Figure
5).
| | Path A | Path B | | , | , | | , | , |
| PDE | 353 K | 276 K | 353 K | 353 K | 276 K | 0.1 MPa | 500 MPa | 240 MPa | 0.1 MPa | 500 MPa | PPGE | 313 K | 253 K | 313 K | 313 K | 253 K | 0.1 MPa | 500 MPa | 400 MPa | 0.1 MPa | 500 MPa | BMPC | 293 K | 233 K | 293 K | 293 K | 233 K | 0.1 MPa | 400 MPa | 290 MPa | 0.1 MPa | 400 MPa | PPG400 | 314 K | 238 K | 251 K | 314 K | 238 K | 0.1 MPa | 500 MPa | 500 MPa | 0.1 MPa | 500 MPa | PVAc | 342 K | 302 K | 342 K | 342 K | 302 K | 0.1 MPa | 450 MPa | 155 MPa | 0.1 MPa | 450 MPa | DGBEA | 293 K | 283 K | 293 K | 293 K | 283 K | 0.1 MPa | 400 MPa | 295 MPa | 0.1 MPa | 400 MPa |
|
|