Use of Wollastonite as a Flux for Bone China Bodies

<table class="table-group" id="tab4"><tr><td><table class="table"><tr><td class="thead-hr" colspan="3"><hr/></td></tr><tr class="thead"><td align="left">Bodies</td><td align="center">Feldspar</td><td align="center">Wollastonite </td></tr><tr><td class="thead-hr" colspan="3"><hr/></td></tr><tr><td align="left">Slip density (g/cm<sup>3</sup>)</td><td align="center">1.796</td><td align="center">1.817</td></tr><tr><td align="left"> Thickness wall-forming in 1<b> </b>min (mm)</td><td align="center">3.58</td><td align="center">3.58</td></tr><tr><td align="left">Viscosity after deflocculation at 0.2<b> </b>wt% of dispersant (mPa<b>·</b>s)</td><td align="center">736.0</td><td align="center">784.0</td></tr><tr class="table-tr"><td colspan="3"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

International Scholarly Research Notices

tab4

Table 4

Table 4: Use of Wollastonite as a Flux for Bone China Bodies 