Modeling of Viscosity and Thermal Expansion of Bioactive Glasses
Table 1
The composition and thermal properties for reference glasses.
| No. | wt% SiO2 | wt% P2O5 | wt% Na2O | wt% K2O | wt% CaO | wt% MgO | Ts (K) | Tg (K) | CTE (10−6 °K) |
| 1 | 45.0 | 6.0 | 24.5 | 0.0 | 24.5 | 0.0 | 784 | 830 | 15.1 | 2 | 44.2 | 6.0 | 23.6 | 6.5 | 12.6 | 7.1 | 722 | 776 | 15.6 | 3 | 44.2 | 6.0 | 17.0 | 4.6 | 18.0 | 10.2 | 789 | 833 | 13.0 | 4 | 44.2 | 6.0 | 10.3 | 2.8 | 23.4 | 13.3 | 800 | 872 | 11.3 | 5 | 49.8 | 6.0 | 15.5 | 4.2 | 15.6 | 8.9 | 795 | 833 | 12.2 | 6 | 52.7 | 6.0 | 17.0 | 4.6 | 12.6 | 7.1 | 803 | 838 | 12.9 | 7 | 52.7 | 6.0 | 10.3 | 2.8 | 18.0 | 10.2 | 804 | 881 | 11.5 | 8 | 54.5 | 6.0 | 12.0 | 4.0 | 15.0 | 8.5 | 821 | 875 | 11.0 | 9 | 56.5 | 6.0 | 11.0 | 3.0 | 15.0 | 8.5 | 830 | 882 | 10.8 | 10 | 61.1 | 6.0 | 10.3 | 2.8 | 12.6 | 7.2 | 837 | 897 | 10.2 | 11 | 67.7 | 6.0 | 8.3 | 2.2 | 10.1 | 5.7 | 838 | 917 | 8.8 |
|
|