Table of Contents
ISRN Corrosion
Volume 2013, Article ID 241830, 7 pages
Research Article

Corrosion Behaviour of Ti-6Al-4V Alloy with Nitride Coatings in Simulated Body Fluids at and

Karpenko Physico-Mechanical Institute, National Academy of Sciences of Ukraine, 5 Naukova Street, Lviv 79060, Ukraine

Received 31 October 2012; Accepted 2 December 2012

Academic Editors: G. Bereket, C.-H. Hsu, and R. Wang

Copyright © 2013 I. M. Pohrelyuk et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.


Nitride coatings were formed on Ti-6Al-4V alloy by thermodiffusion treatment. The corrosion-electrochemical behaviour of Ti-6Al-4V alloy with nitride coatings I and II was investigated in physiological solutions (0.9% NaCl and Tyrode's) at temperatures of and . It is determined that nitride coating I provides Ti-6Al-4V alloy the higher corrosion resistance in Tyrode's solution at both temperatures of solution while nitride coating II in isotonic 0.9% NaCl.