<table>XRD intensity ratios of <i>α</i>-Al<sub>2</sub>O<sub>3</sub>/<i>γ</i>-Al<sub>2</sub>O<sub>3</sub> as a function of annealing temperature. △: nonseeded alumina; ▲: 1% microalumina-seeded alumina; ■: 1% nanoalumina-seeded alumina; ○: 3% nanoalumina-seeded alumina; <svg height="9.0625" id="M3" style="vertical-align:-0.1092pt" version="1.1" viewbox="0 0 10.1 9.0625" width="10.1" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink">
<g transform="matrix(.017,-0,0,-.017,.062,8.863)"><path d="M561 255q0 -109 -78.5 -186t-188.5 -77t-188.5 77t-78.5 186t78.5 186t188.5 77t188.5 -77t78.5 -186z" id="x26AB"></path></g>
</svg>: 5% nanoalumina-seeded alumina.</table>