Effect of Hygrothermal Aging on the Mechanical Properties of Fluorinated and Nonfluorinated Clay-Epoxy Nanocomposites
Table 2
Weight changes in samples after preconditioning.
| Specimens | Absorption, 24 hr (%) | Desorption, 6 hr (%) | Removal (%) |
| Neat EPON 862 | 2.10 | 0.14 | 93.35 |
| 0.5 wt% Nanomer I.28E | 2.09 | 0.40 | 83.65 | 1.0 wt% Nanomer I.28E | 2.15 | 0.42 | 80.33 | 1.5 wt% Nanomer I.28E | 2.13 | 0.44 | 79.56 | 2.0 wt% Nanomer I.28E | 2.20 | 0.45 | 79.35 |
| 0.5 wt% Somasif MAE | 2.14 | 0.32 | 85.18 | 1.0 wt% Somasif MAE | 2.12 | 0.35 | 83.70 | 1.5 wt% Somasif MAE | 2.11 | 0.40 | 81.21 | 2.0 wt% Somasif MAE | 2.13 | 0.45 | 79.07 |
|
|