Synthesis and Characterization of New Optically Active Poly (ethyl L-lysinamide)s and Poly (ethyl L-lysinimide)s
Table 1
Thermal behavior of polymers.
| ||||||||||||||||||||||||||||||||||||
aTemperature at which 5% weight loss was recorded by TGA at a heating rate of 10C/min under air atmosphere. bTemperature at which 10% weight loss was recorded by TGA at a heating rate of 10C/min under air atmosphere. cPercentage weight of material left after TGA analysis at maximum temperature 600C under air atmosphere |