| Polymer | Density | Hardness | Wear resistance on quarz sand | Friction coefficient | | kg/m3 | MPa | min/m | — |
| UHMWPE | 934 | 40 | 18,40 | 0,08 | UHMWPE + Mo | 1150 | 55 | 31,60 | — | PELP (low pressure) | 950 | 55 | 10,50 | 0,10 | PEHP (high pressure) | 900 | 28 | 2,79 | 0,27 | Polypropylene | 850 | 51 | 2,08 | 0,35 | Teflon-4 | 2130 | 38 | 6,36 | 0,05 | Teflon-3 | 2160 | 130 | 5,46 | — | Polystyrene | 1040 | 175 | 0,93 | 0,45 | Polymethylmethacrylate | 1170 | 181 | 1,30 | 0,55 | Polyamide resin | 1080 | 109 | 12,90 | 0,22 | Kaprolone | 1130 | 180 | 3,38 | 0,23 | Vinyl | 1420 | 122 | 3,64 | 0,58 | Polycarbonate | 1180 | 101 | 2,47 | 0,60 | Polyacetal | 1390 | 177 | 1,56 | 0,13 | Epoxy resin | 1270 | 202 | 1,64 | | Wood plastic | 1260 | 312 | 1,30 | — | Fiberglass AΓ-43 | 1850 | 369 | 0,82 | — |
|
|