Studies on the Codeposition of SiC Nanopowder with Nickel, Cobalt, and Co-Ni Alloys
Table 3
Cathodic current efficiency and composition of the deposits.
| Sample | Current efficiency, % | Composition, wt.% | Co | Ni | SiC |
| Co | 98.4 ± 0.1 | 100 | — | — | Co/SiC | 98.6 ± 0.0 | 99.53 | — | 0.47 | Ni | 94.0 ± 0.1 | — | 100 | — | Ni/SiC | 95.1 ± 0.3 | — | 99.97 | 0.03 | CoNi-1 | 96.3 ± 0.1 | 95.05 | 4.95 | — | CoNi-1/SiC | 95.7 ± 0.1 | 94.40 | 5.20 | 0.40 | CoNi-2 | 94.7 ± 0.0 | 91.07 | 8.93 | — | CoNi-2/SiC | 95.3 ± 0.1 | 89.80 | 10.06 | 0.14 | CoNi-3 | 93.8 ± 0.0 | 85.08 | 14.92 | — | CoNi-3/SiC | 94.8 ± 1.0 | 83.95 | 15.87 | 0.18 |
|
|