Residual Stresses Introduced to Composite Structures due to the Cure Regime: Effect of Environment Temperature and Moisture
Table 5
Principal stresses obtained from compression experiments on EP 280 Prepreg.
| Test number | Mechanical stresses [10] | Residual stresses | (MPa) | (MPa) | (MPa) | (MPa) | (MPa) | (MPa) |
| 1 | −77.18 | −253.42 | −95.60 | 5.07 | 4.75 | −5.32 | 2 | −86.29 | −281.52 | −106.37 | 5.07 | 4.75 | −5.32 | 3 | −63.60 | −207.49 | −78.39 | 5.07 | 4.75 | −5.32 | 4 | −66.01 | −227.05 | −84.19 | 5.07 | 4.75 | −5.32 | 5 | −55.62 | −187.58 | −69.57 | 5.07 | 4.75 | −5.32 | 6 | −57.23 | −195.18 | −72.30 | 5.07 | 4.75 | −5.32 | 7 | −53.06 | −191.05 | −67.15 | 5.07 | 4.75 | −5.32 | 8 | −57.59 | −207.38 | −72.89 | 5.07 | 4.75 | −5.32 | 9 | −52.71 | −189.80 | −66.72 | 5.07 | 4.75 | −5.32 | 10 | −49.27 | −198.03 | −64.17 | 5.07 | 4.75 | −5.32 | 11 | −48.49 | −194.87 | −63.15 | 5.07 | 4.75 | −5.32 | 12 | −29.40 | −154.37 | −45.24 | 5.07 | 4.75 | −5.32 | 13 | −24.03 | −126.38 | −37.12 | 5.07 | 4.75 | −5.32 | 14 | −30.58 | −160.81 | −47.23 | 5.07 | 4.75 | −5.32 | 15 | 15.19 | −137.00 | −23.55 | 5.07 | 4.75 | −5.32 | 16 | 13.90 | −125.36 | −21.55 | 5.07 | 4.75 | −5.32 | 17 | 14.73 | −132.91 | −22.85 | 5.07 | 4.75 | −5.32 | 18 | 22.37 | −134.04 | −22.73 | 5.07 | 4.75 | −5.32 | 19 | 20.67 | −126.11 | −21.69 | 5.07 | 4.75 | −5.32 |
|
|