The Effect of Microstructure on Stress-Strain Behaviour and Susceptibility to Cracking of Pipeline Steels

Figure 9

(a) Banding in the as-received grade X65 steel (b) was removed by furnace cooling after 5 hours at 1175°C and then air cooled after 20 minutes at 950°C.
638290.fig.009a
(a)
638290.fig.009b
(b)

We are committed to sharing findings related to COVID-19 as quickly and safely as possible. Any author submitting a COVID-19 paper should notify us at help@hindawi.com to ensure their research is fast-tracked and made available on a preprint server as soon as possible. We will be providing unlimited waivers of publication charges for accepted articles related to COVID-19. Sign up here as a reviewer to help fast-track new submissions.