Mutual Influence of Special Components in Baotou Steel Blast Furnace Slag on the Crystallization Behavior of Glass

<table class="table-group" width="800px"><tr class="fig-image" id="a"><td><img alt="954021.fig.004a" src="https://static.hindawi.com/articles/jm/volume-2012/954021/figures/954021.fig.004a.jpg"/></td></tr><tr class="fig-caption"><td align="center"><table><tr><td><b>(a) </b>Containing 20% slag (crystallization time 1 h)</td></tr></table></td></tr><tr class="fig-image" id="b"><td><img alt="954021.fig.004b" src="https://static.hindawi.com/articles/jm/volume-2012/954021/figures/954021.fig.004b.jpg"/></td></tr><tr class="fig-caption"><td align="center"><table><tr><td><b>(b) </b>Containing 40% slag (crystallization time 1 h)</td></tr></table></td></tr><tr class="fig-image" id="c"><td><img alt="954021.fig.004c" src="https://static.hindawi.com/articles/jm/volume-2012/954021/figures/954021.fig.004c.jpg"/></td></tr><tr class="fig-caption"><td align="center"><table><tr><td><b>(c) </b>Containing 20% slag (crystallization time 2 h)</td></tr></table></td></tr><tr class="fig-image" id="d"><td><img alt="954021.fig.004d" src="https://static.hindawi.com/articles/jm/volume-2012/954021/figures/954021.fig.004d.jpg"/></td></tr><tr class="fig-caption"><td align="center"><table><tr><td><b>(d) </b>containing 40% slag (crystallization time 2 h)</td></tr></table></td></tr></table>

<table>The crystallization state of glass samples containing 20% and 40% blast furnace slag after heat treatment.</table>

Journal of Metallurgy

fig4

Figure 4

Figure 4: Mutual Influence of Special Components in Baotou Steel Blast Furnace Slag on the Crystallization Behavior of Glass 