Columnar-to-Equiaxed Transition in Metal-Matrix Composites Reinforced with Silicon Carbide Particles
Table 3
Predicted and measured CET positions for different composites.
| Experiment number | Alloy and composite | CETpredicted (mm) | CETmeasured (mm) | Relative error (%) |
| 1 | Zn-27 wt.% Al (ZA27) | 91 | 86 | 5.49 | 2 | Zn-27 wt.% Al (ZA27) | 47 | 45 | 4.25 | 3 | ZA27 + 5vol% SiC | 52 | 47 | 9.61 | 4 | ZA27 + 5vol% SiC | 69 | 65 | 5.79 | 5 | ZA27 + 8vol% SiC | 50 | 47 | 6.02 | 6 | ZA27 + 8vol% SiC | 46 | 42 | 8.69 | 7 | ZA27 + 16vol% SiC | 57 | 53 | 7.01 | 8 | ZA27 + 16vol% SiC | 45 | 42 | 6.66 |
|
|