Experimental Study of the Interaction between Recrystallization and Precipitation Processes of an AA8011 Commercial Alloy
Figure 7
Effect of the heating rate on the heat flow. (a) Homogenized samples. (b) Severely deformed samples (from [13]): 5°C/min, 10°C/min, 20°C/min, and ▴ 40°C/min.