Microstructure and Microhardness Evolutions of High Fe Containing Near-Eutectic Al-Si Rapidly Solidified Alloy

Table 1

Average chemical compositions of intermetallic compounds ( and ) observed in high Fe containing near-eutectic Al-Si alloys prepared by rapid solidification as deduced by EDS analysis.

SpecimenPhasechemical composition atomic %
AlFeSi

Al-11Si-11Feα85.0010.464.54
β80.477.9711.56

We are committed to sharing findings related to COVID-19 as quickly as possible. We will be providing unlimited waivers of publication charges for accepted research articles as well as case reports and case series related to COVID-19. Review articles are excluded from this waiver policy. Sign up here as a reviewer to help fast-track new submissions.