Microstructural Characterization and Corrosion Behavior of Electroless Ni-Zn-P Thin Films
Table 2
Elemental chemical composition of deposited thin films.
| Sample | Deposition bath/deposition time | Coating thickness (μm) | Chemical composition (wt.%) | Zn | Ni | P |
| ZNP 1 | A/1 hour | 6.3 | 7.95 | 88.18 | 3.07 | ZNP 2 | A/2 hours | 8.5 | 8.89 | 89.38 | 1.73 | ZNP 3 | B/1 hour | 5.8 | 11.87 | 78.21 | 9.93 | ZNP 4 | B/2 hours | 7.9 | 14.73 | 77.79 | 7.48 | ZNP 5 | C/1 hour | 7.2 | 16.81 | 76.12 | 7.06 | ZNP 6 | C/2 hours | 8.8 | 40.65 | 53.02 | 6.33 |
|
|