Parameter Optimization in the Synthesis of BZT Ceramics to Achieve Good Dielectric Properties

Figure 5

Linear shrinkage and linear shrinkage rate (inset) as a temperature function. The pellets were fabricated from powder calcined at 800°C.
393017.fig.005

We are committed to sharing findings related to COVID-19 as quickly as possible. We will be providing unlimited waivers of publication charges for accepted research articles as well as case reports and case series related to COVID-19. Review articles are excluded from this waiver policy. Sign up here as a reviewer to help fast-track new submissions.