Influence of Cooling Rate on Microsegregation Behavior of Magnesium Alloys
Table 6
Effective partition coefficient for major alloying elements in the investigated alloys.
| Location | AZ91D | AM60B | AE44 | | | | | | | |
| 1 | | | | | | | | Lowest | 0.42 | 0.04 | 0.48 | 0.03 | 0.29 | 0.02 | 0.02 | Highest | 0.58 | 0.50 | 0.68 | 0.73 | 0.42 | 0.14 | 0.15 | Average | 0.53 | 0.21 | 0.56 | 0.30 | 0.34 | 0.07 | 0.08 | 2 | | | | | | | | Lowest | 0.42 | 0.03 | 0.39 | 0.01 | 0.17 | 0.02 | 0.00 | Highest | 0.63 | 0.40 | 0.49 | 0.57 | 0.40 | 0.18 | 0.22 | Average | 0.51 | 0.15 | 0.46 | 0.33 | 0.30 | 0.06 | 0.05 | 3 | | | | | | | | Lowest | 0.44 | 0.08 | 0.36 | 0.03 | 0.31 | 0.02 | 0.02 | Highest | 0.70 | 0.40 | 0.60 | 0.52 | 0.54 | 0.10 | 0.10 | Average | 0.57 | 0.19 | 0.45 | 0.29 | 0.40 | 0.05 | 0.05 | 4 | | | | | | | | Lowest | 0.32 | 0.06 | 0.30 | 0.01 | 0.21 | 0.01 | 0.01 | Highest | 0.56 | 0.36 | 0.47 | 0.23 | 0.33 | 0.13 | 0.07 | Average | 0.41 | 0.18 | 0.36 | 0.11 | 0.27 | 0.03 | 0.04 | 5 | | | | | | | | Lowest | 0.29 | 0.01 | 0.35 | 0.02 | 0.29 | 0.01 | 0.01 | Highest | 0.44 | 0.25 | 0.51 | 0.54 | 0.36 | 0.07 | 0.08 | Average | 0.39 | 0.10 | 0.40 | 0.28 | 0.33 | 0.03 | 0.03 | 6 | | | | | | | | Lowest | 0.33 | 0.03 | 0.31 | 0.01 | 0.19 | 0.01 | 0.02 | Highest | 0.56 | 0.29 | 0.55 | 0.62 | 0.25 | 0.05 | 0.05 | Average | 0.43 | 0.12 | 0.41 | 0.29 | 0.23 | 0.03 | 0.03 |
|
|
Using FactSage software: , , , , and .
|