Optimization for Tribological Properties of Glass Fiber-Reinforced PTFE Composites with Grey Relational Analysis
Table 4
Experimental results and design of experiments using Taguchi.
| Experiment number | Output response | Normalized response | | Wear µm | COF | Wear
| COF
| Wear
| COF
|
| 1 | 226.24 | 0.33 | 0.7364 | 0.4965 | 0.2636 | 0.5035 | 2 | 80.13 | 0.3601 | 0.9146 | 0.3661 | 0.0854 | 0.6339 | 3 | 47.66 | 0.4446 | 0.9542 | 0.0000 | 0.0458 | 1.0000 | 4 | 48.4 | 0.362 | 0.9533 | 0.3579 | 0.0467 | 0.6421 | 5 | 10.1 | 0.4265 | 1.0000 | 0.0784 | 0.0000 | 0.9216 | 6 | 548.21 | 0.3528 | 0.3438 | 0.3977 | 0.6562 | 0.6023 | 7 | 75.3 | 0.4183 | 0.9205 | 0.1140 | 0.0795 | 0.8860 | 8 | 250.41 | 0.35 | 0.7069 | 0.4099 | 0.2931 | 0.5901 | 9 | 81.9 | 0.3749 | 0.9124 | 0.3020 | 0.0876 | 0.6980 | 10 | 32.96 | 0.2943 | 0.9721 | 0.6512 | 0.0279 | 0.3488 | 11 | 40.27 | 0.3587 | 0.9632 | 0.3722 | 0.0368 | 0.6278 | 12 | 830.12 | 0.27 | 0.0000 | 0.7565 | 1.0000 | 0.2435 | 13 | 10.36 | 0.3506 | 0.9997 | 0.4073 | 0.0003 | 0.5927 | 14 | 444.18 | 0.2465 | 0.4706 | 0.8583 | 0.5294 | 0.1417 | 15 | 128.06 | 0.3072 | 0.8561 | 0.5953 | 0.1439 | 0.4047 | 16 | 161.03 | 0.276 | 0.8159 | 0.7305 | 0.1841 | 0.2695 | 17 | 48.6 | 0.2991 | 0.9530 | 0.6304 | 0.0470 | 0.3696 | 18 | 11.91 | 0.3635 | 0.9978 | 0.3514 | 0.0022 | 0.6486 | 19 | 30.51 | 0.2829 | 0.9751 | 0.7006 | 0.0249 | 0.2994 | 20 | 725.06 | 0.2219 | 0.1281 | 0.9649 | 0.8719 | 0.0351 | 21 | 261.31 | 0.2395 | 0.6937 | 0.8886 | 0.3063 | 0.1114 | 22 | 345.77 | 0.2138 | 0.5907 | 1.0000 | 0.4093 | 0.0000 | 23 | 85.73 | 0.2314 | 0.9078 | 0.9237 | 0.0922 | 0.0763 | 24 | 94.65 | 0.2958 | 0.8969 | 0.6447 | 0.1031 | 0.3553 | 25 | 12.91 | 0.2232 | 0.9966 | 0.9593 | 0.0034 | 0.0407 | 26 | 19.01 | 0.2877 | 0.9891 | 0.6798 | 0.0109 | 0.3202 | 27 | 472.97 | 0.2267 | 0.4355 | 0.9441 | 0.5645 | 0.0559 |
|
|