Molecular Dynamics Study on Deformation Mechanism of Grain Boundaries in Magnesium Crystal: Based on Coincidence Site Lattice Theory

<div>Deformation process during tensile test (model J; <svg height="6.1673pt" id="M79" style="vertical-align:-0.2063904pt" version="1.1" viewbox="-0.0498162 -5.96091 5.44961 6.1673" width="5.44961pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M387 375C387 402 357 448 257 448C172 448 82 404 82 326C82 289 108 255 156 241V239C85 223 23 181 23 116C23 39 89 -12 182 -12C265 -12 336 31 378 91L361 114C320 73 269 47 216 47C157 47 115 82 115 137C115 191 160 219 218 219C243 219 262 218 272 217L304 259L302 266C295 265 281 264 255 264C195 264 163 294 163 335C163 377 200 416 249 416C293 416 321 389 329 342C331 332 335 329 341 329C355 329 387 352 387 375Z" id="g113-247"></path></g></svg> is tensile strain in <svg height="6.44133pt" id="M80" style="vertical-align:-0.29774pt" version="1.1" viewbox="-0.0498162 -6.14359 6.59789 6.44133" width="6.59789pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M475 445L452 468C423 436 401 426 385 426S352 427 305 436C268 443 216 448 185 448C156 448 128 425 102 382C89 360 77 338 64 304L89 291C117 340 143 380 190 380C214 380 268 376 295 373C320 370 344 371 362 374L70 101C32 65 23 36 23 18C23 5 27 -3 31 -8C36 -8 39 -6 42 -1C52 15 67 31 80 40S110 49 143 33C195 8 257 -20 290 -20C339 -20 382 11 439 129L416 148C366 74 334 55 305 55C278 55 236 68 203 81C169 94 141 100 122 96C205 170 348 308 411 376L475 445Z" id="g113-123"></path></g></svg> direction. Marked regions are twins found inside grains.)</div>

Journal of Materials

fig10

Figure 10

Figure 10: Molecular Dynamics Study on Deformation Mechanism of Grain Boundaries in Magnesium Crystal: Based on Coincidence Site Lattice Theory 