Phase Transformation of Iron Oxide Nanoparticles from Hematite to Maghemite in Presence of Polyethylene Glycol: Application as Corrosion Resistant Nanoparticle Paints
Table 2
Corrosion rate and corrosion resistance data from polarization curves.
Sample code
Corrosion rate
(mm/y)
Corrosion resistance
(ohm)
Fe
2
O
3
-0 PEG
1.24 × 10
−4
9.2 × 10
5
Fe
2
O
3
-4 PEG
1.04 × 10
−7
2.66 × 10
9
Fe
2
O
3
-8 PEG
2.59 × 10
−8
6.916 × 10
11
Fe
2
O
3
-12 PEG
9.735 × 10
−6
2.541 × 10
7
Microsized Fe
2
O
3
powder
1.574 × 10
−3
4.29 × 10
4
Blank sample
0.4222
225.8