Investigation of Cure Reaction, Rheology, Volume Shrinkage and Thermomechanical Properties of Nano-TiO2 Filled Epoxy/DDS Composites
Table 7
Flexural properties of the epoxy modified nanocomposites.
| | Sample | Flexural strength
MPa | Flexural modulus
MPa | Flexural elongation
% |
| | Neat epoxy | 110 ± 5.5 | 3.3 ± 0.2 | 5.45 ± 0.3 | | 0.7 wt% TiO2 | 91 ± 4 | 3.1 ± 0.1 | 3.74 ± 0.2 | | 3.6 wt% TiO2 | 64 ± 3.7 | 3.5 ± 0.1 | 2.03 ± 0.1 | | 6.9 wt% TiO2 | 77 ± 3.8 | 4.2 ± 0.2 | 2.14 ± 0.1 |
|
|