Effects of Thermal and Solvent Aging on Breakdown Voltage of TPE, PBT/PET Alloy, and PBT Insulated Low Voltage Electric Wire

Table 3

Tensile properties of the thermal and solvent aged polymer specimens.

Sample code	Thermally aged		Thermally aged in solvent
	in air		Toluene		Xylene		TCB		NMP
	Tensile; strength; (MPa)	Elongation; at yield; (%)	Tensile; strength; (MPa)	Elongation; at yield; (%)	Tensile; strength; (MPa)	Elongation; at yield; (%)	Tensile; strength; (MPa)	Elongation; at yield; (%)	Tensile; strength; (MPa)	Elongation; at yield; (%)
TPE1	55±12	754±23	47±6	768±87	48±4	727±75	47±6	734±95	43±6	714±106
TPE1-60°C-6 h	55±11	630±77	46±5	694±142	48±6	681±152	46±7	687±152	45±5	656±69
TPE1-120°C-6 h	52±12	530±63	46±9	568±37	48±11	659±64	44±12	659±73	33±10	425±41
TPE1-180°C-6 h	40±4	180±20	—	—	—	—	—	—	—	—
TPE2	42±8	725±79	43±3	725±80	43±2	695±56	44±3	678±126	39±11	659±17
TPE2-60°C-6 h	52±4	757±79	41±4	673±47	40±1	650±58	38±4	652±55	38±7	614±141
TPE2-120°C-6 h	56±12	761±61	41±6	646±124	40±9	648±50	36±5	636±45	20±10	50±5
TPE2-180°C-6 h	44±4	739±36	—	—	—	—	—	—	—	—
PBT	68±3	497±51	45±6	521±165	46±6	458±135	45±8	484±84	46±4	478±198
PBT-60°C-6 h	62±9	460±38	42±6	378±72	42±9	365±95	39±6	416±170	32±8	461±98
PBT-120°C-6 h	57±6	255±77	43±13	211±68	40±13	215±71	35±6	115±11	28±4	24±5
PBT-180°C-6 h	50±4	29±18	—	—	—	—	—	—	—	—
Alloy	46±4	335±11	52±8	451±109	51±8	463±103	53±6	481±88	61±5	499±77
Alloy-60°C-6 h	46±13	325±44	42±3	391±40	41±6	326±26	31±11	230±199	27±8	127±22
Alloy-120°C-6 h	30±17	19±2	39±5	42±15	34±1	82±30	24±8	29±3	3±0	15±6
Alloy-180°C-6 h	16±11	6±2	—	—	—	—			—	—