Improvement in Contact Strength of Si3N4/SiC Composite by Crack Healing
Table 1
Name of specimen and machining conditions.
| Name | Machining process |
| Smooth | — | Smooth + Healed | Smooth → heat treated |
| #200 | Smooth → #200 grinding | #200 + Healed | Smooth → #200 grinding → heat treated |
| #400 | Smooth → #400 grinding | #400 + Healed | Smooth → #400 grinding → heat treated |
| #400 + Rap | Smooth → #400 grinding → rapping | #400 + Rap + Healed | Smooth → #400 grinding → rapping → heat treated | #400 + Healed + Rap | Smooth → #400 grinding → heat treated → rapping |
|
|
Heat treated at 1300°C, l h in air.
|