Journal of Powder Technology / 2014 / Article / Tab 3 / Research Article
Synthesis, Characterization, and Crystal Structure Refinement of Lanthanum and Yttrium Substituted Polycrystalline 2M Type Zirconolite Phases: Ca1-x Mx ZrTi2 O7 (M = Y, La and x = 0.2) Table 3 Interatomic distances (
) for
ZrTi
2 O
7 and
ZrTi
2 O
7 ceramic powders.
ZrTi2 O7 Ca/Y-O1 2.44859 (15)
Ti1-O1 1.98617 (8) Ti2-Ti2 1.04422 (5) Ca/Y-O2 2.55158 (13) Ti1-O1 2.03767 (9) Ti1-Ti2 2.83723 (12) Ca/Y-O2 2.9158 (12) Ti1-O3 1.87934 (10) Ca/Y-Ca/Y 3.54641 (13) Ca/Y-O3 2.29789 (11) Ti1-O4 2.00482 (9) Ca/Y-Ca/Y 3.67475 (14) Ca/Y-O3 2.49148 (10) Ti1-O5 2.10339 (12) Ca/Y-Zr 3.64459 (14) Ca/Y-O4 2.47791 (14) Ti1-O6 1.86777 (8) Ca/Y-Zr 3.76732 (19) Ca/Y-O5 2.15874 (8) Ti2-O1 2.01446 (8) Ca/Y-Zr 3.52244 (18) Ca/Y-O6 2.35648 (9) Ti2-O2 1.91349 (7) Ca/Y-Zr 3.58109 (14) Zr-O2 2.26148 (10) Ti2-O2 1.60418 (7) Ca/Y-Ti1 3.48736 (19) Zr-O3 2.14917 (9) Ti2-O4 2.02817 (7) Ca/Y-Ti1 3.57798 (17) Zr-O5 2.16485 (10) Ti2-O4 1.51432 (6) Ca/Y-Ti1 3.42492 (17) Zr-O5 2.45348 (10) Ti3-O4 1.99876 (8) Ca/Y-Ti2 3.09889 (15) Zr-O6 2.03887 (11) Ti3-O4 1.99816 (8) Ca/Y-Ti2 3.15781 (18) Zr-O6 2.48648 (9) Ti3-O6 1.94956 (10) Ca/Y-Ti2 3.26467 (18) Zr-O7 2.29685 (12) Ti3-O6 1.94899 (10) Ca/Y-Ti3 3.45802 (17) Zr-Ti1 3.32627 (18) Ti3-O7 1.91452 (7) Ti2-Ti3 2.91319 (14)*2 Zr-Ti3 3.26664 (16) Ti3-O7 1.91774 (7) Zr-Ti3 3.26674 (16) Ti3-Ti3 0.00279 ZrTi2 O7 Ca/La-O1 2.42719 (15) Ti1-O1 1.97120 (9) Ti2-Ti3 2.90539 (15) Ca/La-O2 2.56430 (14) Ti1-O1 2.03661 (9) Ti2-Ti3 2.90580 (15) Ca/La-O2 2.95126 (13) Ti1-O3 1.87550 (11) Ca/La-Ca/La 3.65709 (14) Ca/La-O3 2.27255 (12) Ti1-O4 2.00481 (10) Ca/La-Ca/La 3.56708 (15) Ca/La-O3 2.43456 (10) Ti1-O5 2.09821 (13) Ca/La-Zr 3.60524 (15) Ca/La -O4 2.48768 (15) Ti1-O7 1.86797 (9) Ca/La-Zr 3.81833 (20) Ca/La-O5 2.16519 (9) Ti2-O1 2.00846 (9) Ca/La-Zr 3.46808 (18) Ca/La-O6 2.34869 (10) Ti2-O2 1.91558 (8) Ca/La-Zr 3.61316 (15) Zr-O2 2.27834 (10) Ti2-O2 1.59878 (7) Ca/La-Ti1 3.46905 (20) Zr-O3 2.12595 (10) Ti2-O4 2.02515 (8) Ca/La-Ti1 3.5655 (18) Zr-O5 2.13885 (11) Ti2-O4 1.51705 (6) Ca/La-Ti1 3.37752 (18) Zr-O5 2.45278 (11) Ti3-O4 1.99078 (8) Ca/La-Ti2 3.11141 (16) Zr-O6 2.05856 (11) Ti3-O4 1.99217 (8) Ca/La-Ti2 3.19491 (20) Zr-O6 2.48798 (10) Ti3-O6 1.94159 (11) Ca/La-Ti2 3.29465 (19) Zr-O7 2.28861 (13) Ti3-O6 1.94103 (11) Ca/La-Ti3 3.45485 (18) Zr-Ti1 3.30877 (19) Ti3-O7 1.91666 (7) Ca/La-Ti3 3.45657 (18) Zr-Ti3 3.26337 (17) Ti3-O7 1.91488 (7) Ti2-Ti1 2.83413 (13) Zr-Ti3 3.26234 (17) Ti3-Ti3 0.00249 Ti2-Ti2 1.04354 (6)