Journal of Powder Technology / 2014 / Article / Tab 4 / Research Article
Synthesis, Characterization, and Crystal Structure Refinement of Lanthanum and Yttrium Substituted Polycrystalline 2M Type Zirconolite Phases: Ca1-x Mx ZrTi2 O7 (M = Y, La and x = 0.2) Table 4 O–M–O bond angles in CZTY and CZTLa ceramic powders.
ZrTi2 O7 O1-Ca-O2 60.816 (4) O3-Zr-O7 108.825 (4) O1-Ca-O3 106.177 (5) O5-Zr-O5 76.1297 (26) O1-Ca-O3 69.2880 (31) O5-Zr-O6 159.2397 (19) O1-Ca-O4 170.3787 (8) O5-Zr-O6 120.6788 (25) O1-Ca-O5 64.2639 (28) O5-Zr-O7 69.031 (5) O1-Ca-O6 120.4205 (35) O5-Zr-O6 90.2427 (25) O2-Ca-O3 166.8666 (12) O5-Zr-O6 163.0753 (11) O2-Ca-O3 94.6279 (26) O5-Zr-O7 120.8052 (24) O2-Ca-O4 128.749 (4) O6-Zr-O6 73.0430 (28) O2-Ca-O5 104.9508 (25) O6-Zr-O7 131.759 (4) O2-Ca-O6 71.1752 (31) O6-Zr-O7 71.277 (4) O3-Ca-O3 81.4828 (27) O1-Ti1-O1 176.14021 (30) O3-Ca-O4 64.255 (5) O1-Ti1-O3 94.1837 (28) O3-Ca-O5 65.1166 (23) O1-Ti1-O4 75.3278 (22) O3-Ca-O6 120.2787 (27) O1-Ti1-O5 73.7796 (23) O3-Ca-O4 106.7528 (32) O1-Ti1-O7 94.2665 (27) O3-Ca-O5 109.464 (5) O1-Ti1-O3 89.6886 (27) O3-Ca-O6 82.289 (5) O1-Ti1-O4 105.6577 (21) O4-Ca-O5 110.4121 (30) O1-Ti1-O5 102.3748 (23) O4-Ca-O6 66.510 (4) O1-Ti1-O7 84.6988 (26) O5-Ca-O6 168.09560 (20) O3-Ti1-O4 81.563 (5) O2-Zr-O3 177.13270 (10) O3-Ti1-O5 167.6345 (10) O2-Zr-O5 110.3632 (33) O3-Ti1-O7 100.244 (5) O2-Zr-O5 81.812 (5) O4-Ti1-O5 97.466 (6) O2-Zr-O6 82.7689 (34) O4-Ti1-O7 169.7887 (7) O2-Zr-O6 93.786 (5) O5-Ti1-O7 78.252 (5) O2-Zr-O7 68.158 (4) O1-Ti2-O2 93.158 (4) O3-Zr-O5 68.248 (32) O1-Ti2-O2 88.247 (4) O3-Zr-O5 99.671 (5) O1-Ti2-O4 162.0644 (7) O3-Zr-O6 99.7264 (32) O1-Ti2-O4 86.6597 (35) O3-Zr-O6 85.824 (5) O2-Ti2-O2 89.304 (4) O4-Ti3-O4 71.840 (4) O2-Ti2-O4 102.833 (4) O4-Ti3-O6 84.7296 (33) O2-Ti2-O4 107.853 (4) O4-Ti3-O6 89.5539 (34) O2-Ti2-O4 99.560 (4) O4-Ti3-O7 168.167 (20) O2-Ti2-O4 162.159 (11) O4-Ti3-O7 96.770 (4) O4-Ti2-O4 81.231 (4) O4-Ti3-O6 89.6968 (34) O6-Ti3-O7 92.012 (4) O4-Ti3-O6 84.7067 (33) O6-Ti3-O7 92.953 (4) O4-Ti3-O7 96.865 (4) O6-Ti3-O7 92.615 (4) O4-Ti3-O7 168.27790 (20) O6-Ti3-O7 92.255 (4) O6-Ti3-O6 173.2187 (5) O7-Ti3-O7 94.450 (4) ZrTi2 O7 O1-Ca-O2 60.786 (4) O3-Zr-O7 108.785 (4) O1-Ca-O3 106.177 (5) O5-Zr-O5 76.1597 (26) O1-Ca-O3 69.1780 (31) O5-Zr-O6 159.8997 (19) O1-Ca-O4 170.2887 (8) O5-Zr-O6 120.7988 (25) O1-Ca-O5 64.7539 (28) O5-Zr-O7 69.091 (5) O1-Ca-O6 120.7805 (35) O5-Zr-O6 90.4917 (25) O2-Ca-O3 166.7266 (12) O5-Zr-O6 163.0753 (11) O2-Ca-O3 94.5999 (26) O5-Zr-O7 120.7972 (24) O2-Ca-O4 128.739 (4) O6-Zr-O6 73.0430 (28) O2-Ca-O5 104.7908 (25) O6-Zr-O7 131.389 (4) O2-Ca-O6 71.1852 (31) O6-Zr-O7 71.197 (4) O3-Ca-O3 81.2828 (27) O1-Ti1-O1 176.29021 (30) O3-Ca-O4 64.185 (5) O1-Ti1-O3 94.11737 (28) O3-Ca-O5 65.1866 (23) O1-Ti1-O4 75.1778 (22) O3-Ca-O6 120.1887 (27) O1-Ti1-O5 73.7396 (23) O3-Ca-O4 106.7528 (32) O1-Ti1-O7 94.2965 (27) O3-Ca-O5 109.784 (5) O1-Ti1-O3 89.8686 (27) O3-Ca-O6 82.189 (5) O1-Ti1-O4 105.7977 (21) O4-Ca-O5 110.3411 (30) O1-Ti1-O5 102.4548 (23) O4-Ca-O6 66.480 (4) O1-Ti1-O7 84.5988 (26) O5-Ca-O6 168.08960 (20) O3-Ti1-O4 81.593 (5) O2-Zr-O3 177.28270 (10) O3-Ti1-O5 167.5945 (10) O2-Zr-O5 110.3932 (33) O3-Ti1-O7 100.294 (5) O2-Zr-O5 81.782 (5) O4-Ti1-O5 97.796 (6) O2-Zr-O6 82.7989 (34) O4-Ti1-O7 169.4887 (7) O2-Zr-O6 93.179 (5) O5-Ti1-O7 78.282 (5) O2-Zr-O7 68.189 (4) O1-Ti2-O2 93.186 (4) O3-Zr-O5 68.1975 (32) O1-Ti2-O2 88.191 (4) O3-Zr-O5 99.891 (5) O1-Ti2-O4 162.0784 (7) O3-Zr-O6 99.4584 (32) O1-Ti2-O4 86.1897 (35) O3-Zr-O6 85.489 (5) O2-Ti2-O2 89.189 (4) O4-Ti3-O4 71.179 (4) O2-Ti2-O4 102.846 (4) O4-Ti3-O6 84.7996 (33) O2-Ti2-O4 107.783 (4) O4-Ti3-O6 89.7939 (34) O2-Ti2-O4 99.780 (4) O4-Ti3-O7 168.15820 (20) O2-Ti2-O4 162.1786 (11) O4-Ti3-O7 96.780 (4) O4-Ti2-O4 81.541 (4) O4-Ti3-O6 89.7568 (34) O6-Ti3-O7 92.172 (4) O4-Ti3-O6 84.7847 (33) O6-Ti3-O7 92.483 (4) O4-Ti3-O7 96.685 (4) O6-Ti3-O7 92.615 (4) O4-Ti3-O7 168.17290 (20) O6-Ti3-O7 92.1255 (4) O6-Ti3-O6 173.2485 (5) O7-Ti3-O7 94.7854 (4)